V IEWPOINT

Coatings Attendance is Encouraging!! Judging by events held in February for the coatings community and what is scheduled for March and April, I think things are looking up. The World of Concrete event held in February drew over 55,000 registered professionals and over 1,300 exhibiting companies. PACE 2010 was held in about the same time frame and also seemed to have good attendance this year. NACE is scheduled for mid-March and already is showing over 5,000 registered and 350 exhibiting companies. All in all I think that is a good start to the 2010 year for the industry. Another event held pretty much at the same time was the annual Waterborne Symposium, which is traditionally in New Orleans the week prior to Mardi Gras. The 2010 symposium theme was Advances in Sustainable Coatings Technology – a theme of great importance in today’s envi-

ALL COLORS OF THE RAINBOW ... AND THEN SOME WATERBASED PIGMENT DISPERSIONS STANDARD RESINATED AND NON-RESINATED CUSTOM MADE TO YOUR SPECIFICATIONS

Reitech Corporation

ronment. Despite the travel impact of severe snowstorms that hindered attendees from the northeast, Waterborne still had nearly 200 attendees, 25 presentations and 28 posters. The technology showcase featured 15 exhibitors. For the first time, the symposium also featured a Composites Matrix Workshop, which attracted 60 people. The Shelby F. Thames Best Paper Award was presented to Edwin P. Chan, Kurt A. Page and Christopher M. Stafford from the Polymers Division, National Institute of Standards and Technology for their paper entitled “Harnessing Surface Wrinkling to Measure the Viscoelastic Properties of Polymer Films and Coatings”. The PCI Outstanding Paper Award was presented to Jung Kwon Oh, Bedri Erdem, Jeff Anderson, Kumar Nanjundiah and Jeff Sweeney, Dow Coatings Materials, Dow Chemical Company for their paper entitled “High Throughput Methods for Developing Low-VOC Waterborne Coatings Derived from Polyurethane Dispersions Based on Natural-Oil Polyols”. In addition, Eastman Chemical Company sponsored the USM Best Graduate and Undergraduate Student Poster Awards. It is gratifying to see support for coatings students. We need to encourage young people to pursue a career in the industry. Likewise I think it wonderful to see this publication continue to support an award at Waterborne. Mark your calendar for next year’s Waterborne Symposium which will be held March 2-4, 2011. And of course the big event is coming up on us quickly – this issue of PCI is the Show issue for the American Coatings Show and Conference, both of which will undoubtedly exceed expectations. Nearly 100 highlevel papers have been selected from the several hundred submitted for the conference program. Sixteen focused sessions will be held during three days, including a new session “Science Today – Coatings Tomorrow”. The response from the exhibitor community has been strong, and pre-registrations are high. This event will definitely surpass the 2008 inaugural ACS. So if you haven’t already done so – make you plans and be sure to attend. You cannot afford to miss this!!

For a free brochure call 610-929-9451 or contact us at [email protected] www.reitechcorporation.com Visit ads.pcimag.com

䡲䡲䡲

08084Reitech-rainbow.indd 1 6

006 Viewpoint.indd 6

APRIL 2010 | W W W . P C I M A G . C O M

By Darlene Brezinski, Ph.D. / Editor 7/3/08 11:27:11 AM

3/16/10 3:13:14 PM

I NDUSTRY NEWS

Global Paint Additives Market to Exceed $6 Billion SAN JOSE, CA – According to a new report by Global Industry Analysts Inc. (GIA), the world market for paint additives is projected to exceed $6.0 billion by the year 2015. The trend towards low- or zero-VOC products and the increasing shift towards water-based paint systems are fueling demand for paint additives, providing tremendous growth potential for suppliers of paint and coating additives. The paint and coatings industry has been put under significant pressure by stringent environmental regulations in recent years. In a bid to minimize the impact of their products on the environment, several manufacturers of coatings began reformulating their products. As a result, demand for novel additives that ensure aid in addressing environmental concerns has increased in recent years. The United States dominates the world paint additives market as the single-larg-

est market. The global economic crisis decelerated growth in value demand of paint additives in the United States. Demand for paint additives is expected to revive in the coming years, owing to increasing demand for these products

EPA Increases Transparency Rules on Chemical Risk WASHINGTON, DC – The U.S. Environmental Protection Agency (EPA) has announced a new policy to increase the public’s access to information on chemicals. EPA has announced its intention to reject a certain type of confidentiality claim, known as Confidential Business Information (CBI), on the identity of chemicals. The chemicals that will be affected by this action are those that are submitted to EPA with studies that show a substantial risk to people’s health and the environment and have been previously disclosed on the Toxic Substances Control Act (TSCA) Chemical Inventory. This action represents another step to use the agency’s authority under the existing TSCA to the fullest extent possible. Under the TSCA, companies may claim a range of sensitive, proprietary information as CBI. Under Section 8(e) of the TSCA, companies that manufacture, process or distribute chemicals are required to immediately provide notice to EPA if they learn that a chemical presents a substantial risk of injury to health or the environment. The Section 8(e) reports are made available on EPA’s website. Until now, companies would routinely claim confidentiality for the actual identity of the chemical covered by the Section 8(e) submission, so the public posting of the information would not include the name of the chemical. The new policy ends this practice for chemicals on the public portion of the TSCA Inventory. For additional information on the new policy, visit www.epa.gov/oppt/tsca8e/.

MPI Approval System to be Adopted in Korea BURNABY, Canada – MPI, the institute that establishes architectural paint standards and quality assurance programs in North America, will partner with the Korea Institute of Con8

䡲䡲䡲

008 IndustryNews.indd 8

from formulators in an effort to adhere to changing legislation. Growth in the global market for paint additives is primarily originating from emerging markets such as Asia Pacific. The rapid economic growth in most of the emerging countries in recent years resulted in rampant architectural construction and industrial activity, which created significant demand for paint that, in turn, increased demand for paint additives. Owing to continued growth in architectural construction activity in countries such as India and China, Asia Pacific is expected to emerge as the fastest-growing regional market for paint additives worldwide in the coming years. The report, “Paint Additives: A Global Strategic Business Report,” provides a comprehensive review of market trends, competitive scenarios, product introductions and recent industry activity.

struction Materials (KICM) to test paint and coatings to MPI standards. Carboline Korea and KCC already have products approved by MPI, and more Korean paint suppliers are expected to follow. This will enable facility owners and specifiers with assets in Korea and throughout Asia to access locally sourced paint and coatings approved via a well-proven mechanism for verifying their performance. MPI already has a similar testing agreement with the Paint Research Association in the UK for European paint suppliers. With this new agreement, MPI will have global coverage. Seoul-based KICM is the designated agency for testing, inspection and standards for 41 Korean and international organizations. The agency performs construction-materials testing and research to assure the safety of architectural structures.

U.S. Minerals Sector Declined in 2009 RESTON, VA – According to the U.S. Geological Survey’s recently released report, Mineral Commodity Summaries 2010, the value of U.S. mineral production significantly declined in 2009. The value of raw, nonfuel minerals mined in the United States was $57.1 billion in 2009, a decline of 20 percent over the past year. The value of materials domestically processed and refined from these raw minerals was $454 billion in 2009, a 25 percent decline from 2008. Also over the past year, U.S. dependence on foreign sources for minerals has increased, continuing a trend that has been evident for more than 30 years. The United States relied on foreign sources to supply more than 50 percent of domestic consumption of 38 mineral commodities in 2009 and was 100 percent reliant on imports for 19 of those mineral commodities.


3/16/10 3:11:46 PM

I NDUSTRY NEWS A decline in the U.S. housing market during 2009 caused reductions in the production and consumption of construction materials. Declines in automobile and durable-goods manufacturing resulted in reduced production and consumption of metals including copper, iron, steel, lead and platinum-group metals. The USGS report addresses events, trends and issues in the domestic and international mineral industries and includes statistics on about 90 mineral commodities. It is available at http://minerals.usgs.gov/minerals/pubs/mcs/.

Facility in Boston Harbor. The product, a fast-setting, high-solids epoxy coating, was applied to a gravity thickener at the plant, which is the second-largest watertreatment facility in the United States. The George Campbell Award is given for outstanding achievement in the completion of a difficult or complex industrial commercial coatings project. The Massachusetts Water Resources Authority, owners of the Deer Island plant, and coatings contractor SOEP Painting Corp. of Malden, MA, will receive the award in conjunction with PPG.

SSPC Recognizes PPG With George Campbell Award

PCI Launches Site Dedicated to American Coatings Show

PITTSBURGH – PPG Industries’ Protective and Marine Coatings (PMC) business has been selected as a recipient of The Society for Protective Coatings’ (SSPC) George Campbell Award for 2009-2010. PPG PMC earned the recognition for the performance of its Amerlock 2/400 coating at the Deer Island Water Treatment

TROY, MI – PCI Magazine has introduced a new microsite dedicated to the American Coatings Show. The site, www.pcimag.com/ac_show, includes a schedule of the show, a dining guide for Charlotte, and a blog discussing the latest information about the show. Attendees can get a preview of new products available at the

PCI08081ELCM.indd 1

10

䡲䡲䡲


Visit ads.pcimag.com

show by visiting the microsite’s Online Exhibits. Also available on the microsite is an Exhibitor Info section that gives a list of exhibitors and their booth numbers.

Private U.S. Companies Optimistic About Future SOUTHFIELD, MI – The majority of private U.S. companies are optimistic about the U.S. economy in 2010, according to a global survey of 7,400 private firms in 36 countries. The survey was conducted in November 2009 by Grant Thornton International Ltd. In the United States, private businesses account for an estimated 100 million jobs, more than 70 percent of U.S. employment. In the United States, 51 percent of respondents said that they were optimistic about the U.S. economy in 2010, while 31 percent said they were pessimistic. Globally, 51 percent were optimistic about their respective country’s economy, and 27 percent were pessimistic. The three most optimistic countries were Chile, India and

7/17/08 10:08:44 AM


3/16/10 3:11:54 PM

I NDUSTRY NEWS Australia; and the three most pessimistic countries were Japan, Spain and Ireland. By a two-to-one margin, U.S. private businesses plan to increase their work force rather than decrease it (29 percent verses 14 percent), while 56 percent will keep it the same. Globally, 34 percent plan

to increase their work force, 14 percent plan to decrease, and 50 percent plan no change. Countries with the greatest planned increases were Vietnam (64 percent), Brazil (63 percent) and India (56 percent); the lowest employment increases were planned in Italy (14 percent), Ireland

T

®

H E Patented blending/dispersing blade design makes radical improvement over old saw tooth designs

POLY

STAINLESS

*

Most efficient and aggressive blending/dispersing blade available.

*

Provides proper combination of pumping action and shear/ dispersion essential for fast consistent results.

* * * * *

Built in pumping action cuts processing time.

*

Longer life due to heavier gauge construction. Less heat due to shorter required running time. Excellent for high or low speed and high or low viscosity. Supplied with hubs or mounting holes required to retrofit and upgrade present equipment. Pumping blades without teeth are available and are excellent for gentle blending and agitation. DESIGNERS AND MANUFACTURES OF INDUSTRIAL MIXING EQUIPMENT

Since 1948

CONN

AND

CO., L.L.C.

www.connblade.com

Stirrers Or Complete Units For: PAINTS URETHANE FOAMS ADHESIVES SLURRIES INKS GROUTS CEMENTS ETC. . . .

11 SOUTH MARION STREET • WARREN, PENNA. 16365 • PHONE 814/723-7980 FAX (814) 723-8502

s r

Visit ads.pcimag.com 12

䡲䡲䡲


r

TM

(15 percent), Germany (15 percent) and France (16 percent). In the United States, 51 percent believe that their company’s revenues will rise in the coming year.

ECOAT 2010 Conference Set for May LOUISVILLE, KY – ECOAT 2010 is scheduled to take place May 4-6, 2010, at the Louisville Downtown Marriott, Louisville, KY. The event is an educational conference for people involved in the electrocoat business and for those interested in learning about electrocoating. Three keynote addresses will be offered at the conference. Jeff Oravitz, MetoKote Corp., will kick off the conference with the topic “Manufacturing After the Crisis.” Matt Kirchner, American Finishing Resources LLC, will start day two of the conference by exploring several trends in the U.S. energy sector. For the final keynote of the conference, Steve Schulte, Hixon Inc., will discuss environmental impacts to industrial/electrocoat facilities and practical steps for compliance. Visit www.electrocoat.org/conference for additional information.

Brookfield Offers Training to Maximize Efficiency MIDDLEBORO, MA – Brookfield is offering two courses for users of Brookfield instrumentation. These day-long training sessions give attendees the know-how to verify and improve upon the data required for meaningful research and development and successful quality-control testing. The Practical Course on Viscosity Measurements gives attendees the tools and concepts they need to make the most precise viscosity measurements possible. The course is designed for operators at all levels of experience. The Applied Course on Viscosity Test Methods is designed for the intermediateto-advanced Brookfield instrumentation user in research and development, analytical, and process engineering functions. Focusing on test methods and techniques, it will review and discuss how Brookfield rotational viscometers and rheometers can be used to provide meaningful product analysis. The course takes participants beyond pass/fail criteria, to an understanding of how to apply viscometric data as a problem solving and product performance and processing tool. Visit www.brookfieldengineering.com for course information.


3/16/10 3:12:02 PM

I NDUSTRY NEWS Brookfield has also introduced a new series of online training videos detailing how to verify calibration of viscometers and rheometers. Visit www.brookfieldengineering.com/support/videos.asp to view the videos.

Nano-Engineering Conference Issues Call for Papers ANCHORAGE, AK – ICCE-18, the 18th International Conference on Composites or Nano Engineering, will take place July 4-10, 2010, in Anchorage, AK. The confer-

ence is accepting new paper titles for presentation. Interested authors should submit detailed two-page short papers to David Hui at [email protected]. The conference is looking for new topics in pure and applied science and engineering. All short papers will be reviewed and published as short papers in World Journal of Engineering.

Particles on Surfaces Symposium Solicits Papers

The World’s Most Widely Used Weathering Tester

Accelerate the damaging effects of sunlight, moisture & high temperatures.

r#FTUTJNVMBUJPOPGTIPSUXBWF67TVOMJHIU r.FFUTXPSMEXJEFUFTUNFUIPET r5SVTUFECZDVTUPNFSTXPSMEXJEFGPSZFBST

40 th Anniversary QUV Weathering Tester 1970-2010

Q-Lab Corporation t The Most Trusted Name in Weathering tJOGP!RMBCDPNtXXXRMBCDPN


䡲䡲䡲


HOPEWELL JUNCTION, NY – A call for papers has been issued for the 12th International Symposium on Particles on Surfaces: Detection, Adhesion and Removal. The conference will be held in conjunction with the Process Cleaning Expo in Louisville, KY, on May 4-6, 2010. For more information about submitting a paper for the symposium, contact Robert H. Lacombe, Symposium Chairman, at [email protected].

Deacom Announces ERP Training Schedule WAYNE, PA –The 2010 course schedule for DEACOM® University is now available at www.deacom.net. The schedule will include new course additions, including DEACOM Contact Management. DEACOM University is an accredited ERP training program dedicated to educating users in all areas of the DEACOM Integrated Accounting and Enterprise Resource Planning (ERP) Software System.

Cal Poly Offers Polymers and Coatings Short Course SAN LUIS OBISPO, CA – The Polymers and Coatings program at California Polytechnic State University, San Luis Obispo, CA, will offer a Polymers and Coatings Introductory Short Course during the week of July 19-23, 2010. The one-week course will cover many aspects of coating technology, including resin chemistry, pigments and fillers, additives, VOC testing, application aspects, and rheology. For additional information, visit ww.polymerscoatings.calpoly.edu.

ASTM Offers Online Training WASHINGTON, DC – ASTM International is offering a series of free, one-hour online training workshops that are designed to assist ASTM members. Sessions include Balloting and Handling Negative Votes, Developing and Revising a Standard, Work Item Collaboration Area Training, ASTM Online Training and New Member Orientation. For information, visit www. astm.org/MEMBER_TRAINING/. 䡲


3/16/10 3:12:10 PM

C ALENDAR Meetings, Shows and Educational Programs APRIL 6 Ci4000/Ci5000 Weather-Ometer Workshop www.atlas-mts.com 7 Fundamentals of Weathering Level I www.atlas-mts.com 8 Fundamentals of Weathering Level II www.atlas-mts.com 8-10 CISILE 2010 www.cisile.com.cn/en

18-20 ASC Spring Convention www.ascouncil.org

4-6 ELECTROCOAT 2010 www.electrocoat.org

20-22 Emulsion Polymerization and Waterborne Coatings www.emich.edu/cri

4-6 Particles on Surfaces: Detection, Adhesion and Removal www.mstconf.com

20-22 Logichem 2010 www.logichemeurope.com 30 Understanding Coating Raw Materials www.emich.edu/cri

MAY 4 PSCT May Technical Symposium 12-15 www.psct.org American Coatings Show & Conference www.american-coatings-show.com 4-5 Coatings, Inks and Solvents Technical Advisory Panel 13-16 Meeting PaintExpo [email protected] www.paintexpo.de

5-6 Basics of Polyurethane Coatings www.emich.edu/cri 12-14 NW Coatings Fest 2010 www.pnwsct.whomedia.com/ symposium-ncf 17-21 Introduction to Paint Formulation http://coatings.mst.edu/index.html 18-19 Sink or Swim 2010 www.clevelandcoatingssociety.org 18-20 Appalachian Underground Corrosion Short Course www.aucsc.com

18-20 Advanced Topics in Polymers and Coatings www.emich.edu/cri 19-21 Spray Finishing Technology Workshop www.owens.edu/workforce_cs/ spray2010.pdf 23-26 RadTech UV& EB Technology Expo & Conference 2010 www.radtech2010.com

JUNE 2-4 Principles and Practices of Coating Formulations www.emich.edu/cri 8-10 Improving Durability and Performance of Coatings www.emich.edu/cri

Providing quality products and excellent customer service for 35 years. PRINCIPALS: 3V, Inc. American Talc Company CINIC America Columbian Chemicals Columbia River Carbonates C R Minerals Dianal America Dover Chemical Durez Corporation Elementis Specialties Fawcett Company Frank B. Ross Fuji Silysia Hexion Specialty Chemicals, Inc.

Imerys Instrumental Polymers Technology Kronos LCP Technology Nuroz, LLC Perstorp Reichhold Chemicals Rockwood Pigments Specialty Polymers Taminco TOR Minerals Toyo Ink America Troy Corporation Vitro Minerals Wayne Pigment World Minerals

TCR Industries markets specialty chemicals to manufacturers of coatings, adhesives, inks, sealants, caulks, plastics, building products and allied industries. Our Fine Chemicals Division markets specialty chemicals to manufacturers of food products, cosmetics and personal care products. Our sales geographical territory includes 11 western states and Baja California, serving out of seven warehouses. TCR is practicing "Responsible Distribution" as a proud member of the National Association of Chemical Distributors.

26 Centerpointe Drive La Palma, California 90623 Toll Free: (877)827-1444 www.tcrindustries.com

Visit ads.pcimag.com pci04104TCR.indd 1

16

䡲䡲䡲

016 Calendar.indd 16


3/9/10 11:25:21 AM

3/16/10 3:10:45 PM

C O M PA NY NEWS

Kelly-Moore Receives Green Business Award SAN CARLOS, CA – Kelly-Moore Paint Co. Inc., San Carlos, CA, has received the Green Large Business of the Year award. The company outperformed 100,000 California companies to win the award. Kelly-Moore was selected for its series of recycling programs that diverted 60 percent of its waste and for its ability to motivate employees to commit to recycling efforts. Kelly-Moore was also recognized for its carbon offset program, which resulted in its San Carlos plant being carbon neutral. In 1995, the company developed a safer, more environmentally responsible technique to dispose of leftover paint and became the first paint company in the industry to collect and remanufacture a recycled paint, eCoat. Previously, when half-

used paint cans were returned, the paint and cans were considered unrecyclable waste. Now, Kelly-Moore uses a system that removes the labels and residue from the cans, making them recyclable. The returned paint is sorted by color and type and remanufactured into eCoat. In April 2009, Kelly-Moore started a program to recycle Super Sack storage bags, cut-up plastic totes and other

AkzoNobel Invests in UK Research Hub AMSTERDAM, The Netherlands – AkzoNobel is investing almost €10 million to enhance its Felling, UK, site. A fire-protection testing laboratory and a polymer lab for powder coatings are being added to the existing R&D infrastructure at the site. Due to be completed early next year, the testing lab will be used by the company’s Marine & Protective Coatings (M&PC) business to develop fire-protection coatings. The new polymer lab will allow researchers at AkzoNobel Powder Coatings to handle and develop new materials; it will also include scale-up capability and an application line.

Huntsman Amines Bridge Gap in Chinese Rail Project EVERBERG, Belgium – A series of concrete bridges that support a new high-speed rail line connecting Beijing and Shanghai is set to benefit from the protective properties of specialty polyetheramines from the Performance Products division of Huntsman Corp. The Chinese Ministry of Railways is building an 800-mile dedicated passenger rail link to ease pressure on one of China’s busiest transport routes. The route crosses the Yellow River and the Yangtze delta. Because of the soft terrain in this area and the need to minimize land usage, almost 80 percent of the line is being built on metal and concrete bridges that are compatible with the transportation system already in place. It is on these structures that Huntsman’s polyetheramines will be used. JEFFAMINE® D-2000, JEFFAMINE T-5000 and JEFFAMINE D-400 polyetheramines have been used to create a polyureabased coating that is being sprayed onto the bridges’ concrete 18

䡲䡲䡲

018 Company News.indd 18

previously unrecyclable containers. The program resulted in a 10-15 percent reduction in landfill waste. Additionally, Kelly-Moore’s factory management developed a collection system for rainwater to offset water usage and built a berm around the manufacturing plant to prevent any possible paint spillage from getting into the local creek. Kelly-Moore has continued to green its manufacturing facility. It has replaced old HVAC units with energy-efficient ones, installed a new dust collector that reduced plant noise levels and energy consumption by approximately 50 percent, enrolled in a program to buy carbon offsets, and captured waste heat generated from the plant’s large compressor and now uses it to heat an adjacent building.

slabs, which act as a hardwearing base for the ballast-less tracks. Forming a waterproof protective layer, the coating will guard the concrete against weather, abrasion, and general wear and tear.

Columbian Chemicals Expands TCR Industries’ Territory LA PALMA, CA – Columbian Chemicals, Marietta, GA, has expanded TCR Industries’ territory to represent Columbian’s Raven® industrial carbon blacks. The expanded territory covers 11 western states through seven warehouses. The territory includes California, Oregon, Washington, Idaho, Montana, Wyoming, Utah, Nevada, Colorado, New Mexico and Arizona. TCR Industries is authorized to promote Columbian carbon black products in the paint and coatings, inks, plastic, and construction markets.

Daimler Chooses GREENKOTE Coating Process CLEVELAND – GREENKOTE® Plc, a global coating technology company headquartered in Cleveland, will provide corrosion protection for selected Daimler automotive parts beginning in the first half of 2010. Initial orders include components for passengersafety-related applications. Additionally, Daimler is finalizing technical approval of GREENKOTE as one of its suppliers of zinc diffusion coatings, using the company’s patented thermo-diffusion coating process. GREENKOTE is a thermal-diffusion coatings process that modifies and improves the basic surface characteristics of metals and is applicable to metal finished parts in many industries.


3/16/10 2:55:19 PM

C O M PA NY NEWS AkzoNobel Powder Coatings to Supply Ingersoll Rand

Malvern Instruments Opens Center of Excellence in India

MONHEIM, Germany – Cognis has announced recipients of its internal Innovation Award. The award recognizes teams responsible for innovative and successful projects. The Gold Award went to a team from the Functional Products strategic business unit (SBU) for Emgard FE, a fuel-efficient axle lubricant for heavy-duty trucks. The Silver and Bronze Awards went to two teams from the Care Chemicals SBU. Silver was given to the employees behind Plantapon LGC Sorb, a new environmen-

MALVERN, UK – Malvern Instruments has opened a third center of excellence in India, established through its joint-venture company Malvern Aimil Instruments Pty. Located in Delhi and designed to serve customers in the north and northeast of India, the new center of excellence houses laboratories that are equipped with a range of Malvern systems and staffed by a full-time applications team. The team will provide demonstrations and deliver training, applications and technical support, as well as sample analysis.

$PHULFDQ&RDWLQJV6KRZERRWK1R

Cognis Recognizes Innovative Employees

AMSTERDAM, the Netherlands – AkzoNobel Powder Coatings has entered into a three-year agreement with Ingersoll Rand that makes it the preferred global supplier for powder coatings. AkzoNobel will supply powder coatings to Ingersoll Rand through its brand, Interpon Every Color Is Green.

tally sound anionic surfactant based on alkyl polyglycosides technology. Bronze went to the developers of a customized Euperlan pearlizer concentrate. Finally, the Special Category Award, which was presented for the first time this year, was won by a team that implemented a package of measures to improve the ether sulfate production process.

70 2[\OLQN )RUEHWWHU ZDWHUERUQH FRDWLQJV

%H*UHHQDQG%HWWHU 7KHSHUIRUPDQFHDGGLWLYHIRU Ŷ 6WURQJHU ZDWHUERUQHFRDWLQJV Ŷ )DVWHU GU\LQJ Ŷ %HWWHU EORFNLQJUHVLVWDQFH Ŷ +LJKHU KXPLGLW\UHVLVWDQFH Ŷ 5HGXFHG GLUWSLFNXS &DOOXVIRUDIUHHVDPSOH 2[\OLQN#EXKOHUJURXSFRP 86$&DQDGD (XURSH$VLD ZZZEXKOHUJURXSFRP


䡲䡲䡲


Hockmeyer Equipment Granted Fifth Patent HARRISON, NJ – Hockmeyer Equipment’s fifth patent covering immersion mill enhancement has been granted by the U.S. government. The patent covers the deterrence of wear at a bearing construct in a basket media mill. The device involves the introduction of slots in the rotating peg hub within the basket. As the hub rotates, centrifugal force pulls the media and feedstock away from the polymer-bearing construct within the peg hub. This creates two favorable conditions. One result is extended bearing life regardless of the media type or size; the other is the elimination of micro media escaping through the clearance between the rotating drive shaft and the bearing construct. Bearing life, typically six months to one and a half years, has more than doubled.

BASF Expands Superior Materials’ Distribution Agreement GARDEN CITY, NY – BASF Corp. has announced an expansion of Superior Materials Inc.’s distribution responsibilities. For customers in the plastics industry, Superior Materials Inc. will now be responsible for sales of BASF’s pigments, colorants, dyes and additives portfolio in New York, New Jersey and Connecticut. For customers in the coatings, sealants, adhesives, elastomers and ink industries, Superior Materials Inc. will be responsible for sales of pigments, colorants, dyes, dispersions and Uvinyls® in New York, New Jersey, Connecticut, Maryland, Delaware, Washington D.C. and Pennsylvania east of Harrisburg. Superior Materials Inc. will also be responsible for sales of Attapulgite additives in New York, New Jersey, Connecticut, Pennsylvania, Virginia, West Virginia, Maryland, Delaware and Washington D.C.

Nevada DOT Approves Seicoat Corp. Coatings LOS ANGELES – A line of anti-graffiti coatings from Seicoat Corp. has recently been approved and added to the Qualified Products List by the Nevada Department of Transportation. The products are GPA-200 Graffiti Proofer ® Anti-Stick and GPA-300 Graffiti Proofer Non-Stick anti-graffiti coatings. The GPA-200 coating is extremely durable and causes most paints to simply run off the film. The GPA-300 product


3/16/10 2:55:28 PM

allows anyone to remove graffiti with a dry cloth or water rinse without the use of any cleaning chemicals. The coatings are clear, UV stable, chemical and abrasion resistant, and provide true non-stick surfaces that resist paint, permanent markers, stickers and adhesives.

Siltech Acquires Rhodia Manufacturing Facility TORONTO – Siltech Corp. has acquired Rhodia’s manufacturing facility in Mississauga, Ontario, Canada. The 113,000-square-foot plant is equipped with highly specialized chemical reactors, bulk storage and railroad facilities. Siltech will retain Rhodia’s employees and will continue to manufacture Rhodia’s products under a long-term contract. Siltech’s present manufacturing and research facility in Toronto, Canada, will continue to operate as the company’s headquarters.

Hexion Specialty Chemicals Plans Monomer Plant in Korea COLUMBUS, OH – Hexion Specialty Chemicals Inc. has approved construction of a manufacturing plant in Onsan, Korea, to produce Cardura™ monomer, a glycidyl ester derivative of Versatic Acid 10. The plant will be constructed within an existing Hexion manufacturing complex in Onsan. Construction of the new facility will begin in the first quarter, and completion is slated before the end of this year.

Bring on all your bright ideas. Our global UV/EB resources help make them winners. Wherever you need UV/EB support, Sartomer is there for you – in the Americas, Europe, and Asia. We deliver leading-edge UV/EB technology and responsive local manufacturing. We can also help with the complexities of product/country registration issues. Our in-depth expertise and high-performance specialty chemicals will help you bring all your ideas to life and get them to market – fast. Now you can take on any job – plastic and metal coatings, inks, display, automotive, adhesives – or even a totally new application. Rely on us from initial concept to final delivery.

Hexion to Sell Solventborne Coating Resins Business COLUMBUS, OH – Hexion Specialty Chemicals Inc. has signed a definitive agreement to sell its Italian solventborne alkyd and polyester coating resins business to an affiliate of Tenax Group, an Italian-based company that produces similar products. The sale will include all aspects of the business, including a production facility in Cola di Lazise, Italy. The sale represents Hexion’s exit from the European solventborne coatings market. Hexion continues to fully participate in the waterborne, powder coatings and coating resins markets, both in Europe and globally.

Formulators choose Sartomer for UV/EB innovation and consistent quality… batch after batch. Our broad line of more than 500 monomers and oligomers leads the world. If your formulation calls for something unique, we tailor a custom fit. Contact us now for the help you want to beat the competition. Call 800-SARTOMER, 610-363-4100 or visit www.sartomer.com.

Visit us at RadTech 2010

Baltimore, MD; May 24-26, Booth 309

Eastman Acquires Specialty Polymers Facility in China KINGSPORT, TN – Eastman Chemical Co. has completed the acquisition of Tongxiang Xinglong Fine Chemical Co. Ltd., a cellulose-based specialty polymers manufacturing facility located near Shang-

Visit ads.pcimag.com PA I N T & C O AT I N G S I N D U S T RY


䡲䡲䡲

21

3/16/10 2:55:35 PM

C O M PA NY NEWS hai, China. The acquisition will support Eastman’s Coatings, Adhesives, Specialty Polymers and Inks segment, specifically its Ensure™ product line, by providing additional capacity to meet the growing demand in China.

Arkema Integrates Acrylics Assets From Dow CARY, NC – Arkema has formally completed its acquisition of Dow’s Acrylic Monomers and Acrylic Latex Polymers (UCAR Emulsion Systems) business in North America.

::: Intelligence in Rheometry

Rheometry Focusing on Solutions

The acrylic monomers production site in Clear Lake, TX, is being integrated into Arkema’s existing Acrylics business unit, within the Industrial Chemicals business segment. The acrylic latex polymers activity forms a new business unit, Arkema Emulsion Systems, which is dedicated to the paint, coatings, adhesives and construction-product markets. This new business unit will be part of the Industrial Chemicals business segment. Richard Jenkins has been appointed President of this newly created business unit. Jenkins was previously the General Manager of Dow’s UCAR Emulsions Systems and Monomers business. Arkema Emulsion Systems is headquartered in Cary, NC, and operates three latex production facilities in California, Illinois and Louisiana. Research and development, marketing, sales and administration functions are located at the North Carolina headquarters. The Polyphobe™ rheology modifiers formerly in the UCAR Emulsion Systems product line are being integrated into Arkema’s Coatex subsidiary. The integration will extend Coatex’s portfolio for the paint and coatings industry to the United States, Canada, Mexico and Puerto Rico markets.

BASF Venture Capital Invests in Quantiam Technologies LUDWIGSHAFEN, Germany – BASF Venture Capital GmbH, Ludwigshafen, Germany, is investing in Quantiam Technologies Inc., Edmonton, Canada. Quantiam Technologies develops and markets functional coatings for extreme operating environments such as petrochemicals industry applications. Quantiam will use the additional capital to fund further growth. A major focus of the investment will be catalytic surface coatings known as catalyzed-assisted manufacture of olefins or CAMOL.

Fully automated, robotically operated: The HTR High Throughput Rheometer from Anton Paar.

Flint Group to Acquire Torda

³ Automatic sample filling and cleaning of measuring systems ³ Processes up to 96 samples in a single run up to 24 hours

Anton Paar® USA

³ Modular setup, flexible to individual applications ³ All standard MCR 301 test types, configurations and accessories apply

800-722-7556 [email protected] www.anton-paar.com

LUXEMBOURG – The Flint Group has signed an agreement to acquire Torda, a manufacturer of printing inks for the packaging markets in northern Europe, the Balkans and the Middle East, with a substantial presence in Eastern Europe. This acquisition is the third step Flint Group has taken within the last 12 months to foster its expansion in Eastern European markets. 䡲

Visit ads.pcimag.com

䡲䡲䡲

PCI03094ANTN.indd 1

22



2/3/09 9:55:41 AM

3/16/10 3:17:00 PM

N AMES IN THE NEWS 䡲 Patrice Barthelmes has been appointed CEO of Eliokem, a worldwide specialty chemical company. Barthelmes served as Vice President and Director for the Packaging & Building Materials division of Rohm & Haas, a position he held from 1999 until 2009, when Dow purchased Rohm & Haas. In 2009, he was appointed Vice President and Group Director for Dow’s AdheBarthelmes sives & Functional Polymers division. 䡲 Kristopher Felice has joined CAS-MI as a Chemist/Coatings Technologist. In his new role, Felice uses a wide range of analytical techniques, such as SEM/EDXA, FTIR, ATR, Microscopic FTIR and MDSC. He also has expertise in paint and coatings physical testing, as well as failure analysis.

䡲 Scott Harris has been promoted to the position of Operations Manager at Thermcraft Inc. Harris has over 25 years of manufacturing experience. 䡲 Jeff Hartel

has joined NSL Analytical Services Inc. as Account Manager for metallurgical and mechanical testing. Hartel will assist with business development activities. He will also introduce NSL’s elemental chemical analysis capabilities to metallurgical and mechanical testing customers.

䡲 NanoHorizons Inc. has appointed Chris Haupt to the newly created position of Vice President, Industrial Business Unit. Haupt’s professional focus and expertise are in polymer chemistry and business development for the C.A.S.E and flexible-foam markets. 䡲 Timothy M. Knavish has been appointed Vice President, Automotive Coatings, Americas, for PPG Industries. He will report directly to Cynthia A. Niekamp, Vice President, Automotive Coatings. 䡲 Malvern Instruments

has appointed Terry Liu to the role of Process Specialist. Liu is part of the Malvern China team and works from the company’s Shanghai office. He will support customers across a range of industries in their implementation of Insitec in-, on- and at-line solutions for particle-size measurement and process optimization.

Liu

䡲 Joan A. Schuller has been named General Manager for the North

American region of Dow Coating Materials. In her role, Schuller is responsible for setting the business strategy and leading the North American Leadership Team.

䡲 H. Morgan Smith has been named the Chairman of the Board of

Van Horn, Metz & Co. Inc. Barrett C. Fisher III has assumed the role of President, and Brian Boorman has been named the Executive Vice President.

䡲 Superior Materials Inc. has hired Peter Zillitto as Regional


䡲䡲䡲

024 Names.indd 24

Sales Manager, Mid-Atlantic. Zillitto will be responsible for the sale of BASF pigments, colorants, additives and Attagel® products in eastern Pennsylvania, Maryland and Delaware, along with Attagel in all of Pennsylvania, Virginia and West Virginia. He will also sell Imerys, Evonik, Akzo Nobel, Kronos, DayGlo and Schlenk products. 䡲


3/16/10 2:49:29 PM

Nanocomposite for High-Performance Fabrics

I

nflatable fabrics are used in a number of different applications, such as automotive airbags, parachutes, rafts, hot air balloons and inflatable structures for space exploration. An inflatable fabric consists of a base fabric that provides strength and a multifunctional coating layer. Besides blocking pores in the fabric and providing impermeability, the coating imparts flexibility, toughness and tear strength to the fabric. In addition, the coating protects the fabric from the heat generated during inflation and provides smooth deployment. A desirable coating material should have low permeability, good adhesion to the fabric and good mechanical strength. The first generation of inflatable fabrics was based on nylon 6,6 fabric with a neoprene coating. However, neoprene had several shortcomings, including necessarily thick coatings, a tendency to stick when deployed, limited environmental stability and marginal thermal resistance. As improvements in nylon 6,6 and alternative fabrics continue, silicone coatings are being used more often than neoprene coatings to: (a) protect the fabric from heat-scorching; (b) allow thinner and more foldable coated fabrics; (c) improve long-term environmental stability; and (d) provide better compatibility with nylon. Silicone coatings are increasingly used on inflatable fabrics in several consumer, military and space applications. An excellent example is the successful deployment of the airbag system for the Mars Pathfinder. Silicone coatings exhibit one to two orders of magnitude less atomic oxygen erosion compared to their organic counterparts in low earth orbit.1 Notwithstanding their excellent long-term thermal stability, weatherability and flexibility, silicone coatings are relatively weak compared to other elastomers. Fillers, such as amorphous silica, are often added to the matrix to reinforce the network. Another drawback of silicone material is its poor adhesion to the substrates because of its low surface energy. These problems can be addressed by nanotechnology, and indeed various attempts have been made using nanoscale additives to strengthen the silicone and reduce gas permeability. This article introduces a commercially viable nanoscale additive developed by NEI Corporation that improves fabric tear strength, tensile strength and hardness at low additive loadings. At the same time, the NEI product greatly improves adhesion between the silicone and the fabric. The NEI product is a nanoscale additive package that is easily added to commercial silicone coating formulations to impart excellent coating properties. The first part of this article discusses how nanoscale additives can be used to improve the properties of the sili-

cone base polymer. The second part presents data on NEI’s nanoscale additive-reinforced silicone-coated fabric.

Forming Silicone Nanocomposites In recent years, polymer nanocomposites have received significant attention since nanoscale particles provide an opportunity for enhancing the mechanical and functional properties of the polymer at relatively low-volume fractions, thereby preserving the desirable properties of the polymer, such as flexibility and ductility. The reasons for using nanoscale particles in a polymer matrix are outlined in the following points. 1. Incorporating nanoscale particles, particularly those with a high aspect ratio (e.g., platelet-shaped clay nanoparticles) in a polymer matrix leads to several beneficial features, including low percolation threshold (< 2 vol%), high interfacial area and a size scale that is comparable to that of polymeric molecules. 2. The interface between surface-modified nanoparticles and the polymer matrix will be smooth, resulting in effective load transfer to the matrix and a smooth surface finish to the final nanocomposite. Conversely, coarse particles, because of their large size and particularly when added in large volume fractions, do not bond well with the polymer matrix. Consequently, coarse particles degrade the mechanical properties of the base polymer. 3. Incorporating solid particles (or nanoparticles) in a polymer matrix or in a polymer-based coating formulation can give rise to processing issues such as a significant change in viscosity, inhomogeneous mixing and reduction of shelf life. All these problems can degrade the final properties of the nanocomposite. Nanoparticles present less of a problem than micon-sized particles because nanoparticles can be added in much smaller quantities to achieve a similar reinforcing effect. Additionally, when nanoparticles are modified with a suitable organic molecule/oligomer, they become compatible with the matrix and ameliorate processing problems. Silicones, also referred to as polysiloxanes or PDMS, have the repeating unit [Si(R)2-O]- and are prepared from chlorosilanes. Depending upon the number of repeating units in a polymer chain and the degree of crosslinking, several different types of commercial silicone products can be produced: fluids, emulsions, compounds, lubricants, resins and elastomers or rubbers. The silicone material discussed in this article is a silicone elastomer, suitable for use as an inflatable fabric coating. Nanoscale additives in silicone coatings offer the opportunity to improve physical gas barrier properties, in addition to enhancing mechanical properties. Some data indicates that oxygen transmission rates for nanocompos-

By Kenneth Eberts, Runquing Ou and Kunal Shah | NEI Corporation, Somerset, NJ 32

䡲䡲䡲

032 NEI FT.indd 32


3/16/10 2:47:04 PM

Coatings ites of silicone are usually less than half that of the unmodified polymers. The aspect ratio of the additive nanoparticles has been shown to have a major effect on enhancing gaseous barrier properties, particularly with higher aspect ratios.2 Researchers at Argonne National Laboratory demonstrated that the oxygen barrier properties of nanocomposite films were 200,000 times better than oriented propylene and over 2,000 times better than Nylon-6.3 Researchers at NASA showed that by adding about 2 vol% additives in a thermoplastic matrix, the hydrogen permeability can be reduced by 10 to 20%.4

Experimental Procedures An example of the wide variety of airbag applications is the Mars Pathfinder airbag system. With funding provided by NASA, we chose to work with materials similar to those used for this Mars mission. Dow Corning Liquid Silicone Rubber (LSR 3730) was used as the base silicone material. It is a two-component, fumed silica-filled, high solids (>98%) vinyl-addition (platinum catalyzed), hightemperature-curing (150-200 °C) silicone with high viscosity (165,000 cSt). This is a commercial coating formulation optimized for adhesion to fabrics and is chemically similar to the silicone rubber used to coat the Mars Pathfinder airbags (i.e., Silastic LT-50, a Dow Corning product designed for enhanced low temperature performance). The fabric used was Vectran, a commercial woven fabric obtained from Fabric Development, Inc. NEI nanoscale additives, hereafter called Nanomyte™ PC-30, were prepared by modifying the surface of inorganic nanoparticles with organic functional groups that can react with the silicone matrix, thereby facilitating dispersion and allowing chemical bonding of the nanoparticles with the matrix. The functional groups also improve the adhesion of the silicone coating with the fabric. Nanomyte PC-30 was mixed thoroughly with part B of LSR 3730 before mixing with part A and catalyst. The mixed, uncured silicone resin was then applied to Vectran fabric and cured at 190 °C, followed by aging at 120 °C. This coating and curing process was then repeated to apply a second coat. Coated Vectran sheets were cut to the standard geometry as specified in MIL-C-21189(Aer) TM 10.2.4 for cutslit tear testing. Samples were tested on a CRE-type tensile machine using hydraulic/pneumatic grips. Peel testing was conducted according to ASTM D 187601, Standard Test Method for Peel Resistance of Adhesives (T-Peel Test) using an MTS QTest/25 Elite Controller frame

fitted with a 5kN load cell and rubber-faced, manual grips. To prepare T-Peel test samples, uncured coating material was applied to the coated faces of two cured, coated Vectran sheets using a drawdown process. The sheets were then laid face-to-face to make sandwiched sheets, which were compressed together and cured. Spherical test articles, 18” in diameter, were fabricated at ILC Dover (a leading manufacturer of high-performance softgoods, and a collaborator on this project) for leakage testing (Figure 1). The test articles were inflated to 1, 2 and 3 psi, and the leak rate was measured. This was followed by holding the inflation pressure at 5 psi, then reducing the pressure and repeating the leakage tests at 3, 2, and 1 psi.

Nanoscale additives in silicone coatings offer the opportunity to improve physical gas barrier properties, in addition to enhancing mechanical properties. FIGURE 1 | Pressurization testing of 18” test spheres at ILC Dover.

PA I N T & C O A T I N G S I N D U S T R Y

032 NEI FT.indd 33

䡲䡲䡲

33

3/16/10 2:47:16 PM

Nanocomposite Coatings for High-Performance Fabrics

Results and Discussion Figure 2 shows the results from cut-slit tear testing. The coated fabric containing Nanomyte PC-30 exhibits significantly improved tear strength. Examination of the tested samples revealed that different degrees of delamination of the silicone coating material from the fabric had occurred as a result of the tearing action (Figure 3). In general, there appeared to be substantial delamination of coating material from the Vectran for control samples, especially at the grip points and along tears. This delamination is an adhesive failure. The samples containing Nanomyte PC-30 exhibited minimal or no delamination. Further, in some cases, residual coating material remained connected to exposed yarns within the tear zone giving a “toothed”

appearance, offering evidence of a cohesive failure; this was not observed to such a degree for control samples, where yarns were typically stripped bare. The above tests demonstrate the importance of adhesion between the fabric and coating, which is promoted by Nanomyte PC-30. Further evidence of stronger adhesion is shown by the T-Peel test. Figure 4 shows a strong correlation between Nanomyte PC-30 loading and adhesive strength. In addition to enhancing coating-fabric adhesion and mechanical strength, Nanomyte PC-30 greatly suppresses leakage in fully sealed test articles. Figure 5 shows a strong trend towards reduced test article leakage for spheres manufactured with the nanocomposite material versus control.

FIGURE 2 | Averaged tearing strength of coated fabric with and without 1.5 wt% Nanomyte PC-30.

FIGURE 4 | Averaged peel resistance data for self-adhesion of coating formulations. 45 40

650

35 Peel Resistance (N)

Average Tearing Strength (lbs)

700

600

550 500

30 25 20 15 10

450

5 0

0

400 Control

Nanomyte™ PC-30

FIGURE 3 | Macro photograph of cut-slit tear samples along the tear.

FIGURE 5 | Graph of leak rate during pressure testing of optimally sealed test articles. 400

Nanomyte™ PC-30

Coated Yarns

Bare Yarns

Leakage Rate (sccm)

Control

3 6 Nanomyte™ PC-30 (wt%)

350

Nanomyte™ PC-30 (1.5wt%)

300

Control

250 200 150 100 50 0

Delamination

34

䡲䡲䡲

032 NEI FT.indd 34

1

2

3 3 Pressure (psi)

2

1


3/16/10 2:47:26 PM

Nanocomposite Coatings for High-Performance Fabrics

…the mechanical strength and coating-fabric adhesion can be significantly enhanced by adding relatively low levels of nanoparticles. Conclusions We have shown that the mechanical strength and coating-fabric adhesion can be significantly enhanced by adding relatively low levels of nanoparticles. Certain fabric coatings that are used for space applications are formulated with fillers, including metal oxide particles, in order to increase strength. However, these additives typically require high additive loading in order to attain the desired properties, which can adversely impact the weight of the part and potentially result in degradation of mechanical properties. Our approach permits the use of far lower levels of additive loading, which better preserves the material’s desirable characteristics. Further, NEI’s nanoscale additives significantly suppress air leakage in

the test articles fabricated. Most importantly, NEI’s technology has a minimal impact on the coating application process. That is, NEI’s patent-pending technology can be readily incorporated into commercially available coating formulations and requires no special processing or equipment when applied to the fabric. In addition, using the NEI nanoparticle additive approach, other desirable functionalities can be engineered into the coating formulation. 䡲

Acknowledgments NEI Corporation is grateful to the NASA SBIR program for funding this Phase II effort, which was carried out under contract NNL07AA11C. The authors wish to thank Ms. Robin C. Hardy of NASA Langley Research Center, Virginia, for her constant encouragement and suggestions during the Phase II program. The authors also wish to thank Ms. Jody Ware of ILC Dover for her support of this development work, particularly with respect to prototype airbag fabrication and testing.

References 1 2 3 4

Dworak, P; Soucek, M. D. Progress in Organic Coatings 2003, 47, 448. Takeuchi, H.; Cohen, C. Macromolecules 1999, 32, 6792. http ://w w w.anl.gov/techtransfer/pd f/Nanocomposite4-7-03.pdf. www.grc.nasa.gov/www/RT2001/5000/5150campbell.html.

For more information see www.neicorporation.com or email [email protected].


䡲䡲䡲

032 NEI FT.indd 36


3/16/10 2:47:34 PM

The World Marketplace for Protective Coatings –

T

he past 35 years have brought massive changes to the protective coatings industry. Increasing levels of regulatory oversight and the reduction in VOC emissions are among the more obvious impacts. The industry also faced a shift in markets, as China, Dubai and other world areas made significant investments in infrastructure to support economic development. However, change is also a reaction to the global trends occurring throughout the world: population growth, globalization/urbanization, climate change/global warming, the healthcare revolution and accelerated technology changes. All of these trends have and will continue to create new opportunities. How can our business model recognize and take advantage of these trends that create coatings opportunities?

Sowing the Seeds of Change: 1970s – 1990s Evolving Regulations In the 1970s, heightened environmental awareness galvanized organizations and individuals into action, culminating in unprecedented changes for the protective coatings industry. The first truly game-changing seeds of change were sown with the Consumer Product Safety Commission’s 1978 ban of lead-based paint in the United States. This caused a ripple effect that increased the scrutiny of the use of lead-based paint in other countries. To fully appreciate the impact, it’s important to remember that lead-based paint (oil alkyds) had been used as a universal coating for a thousand years, and was a dominant

3 38

䡲䡲䡲

038 Bayer FT.indd 38

coating for bridges, ships, infrastructure and other industrial – not to mention consumer – applications in industrialized nations. Soon thereafter, the industry faced another major challenge: sweeping regulations focused on lowering volatile organic compounds (VOCs). Space does not permit a detailed discussion into the regulatory environment taking place during this time. However, it is possible to briefly summarize some of the key milestones. In the 1980s, some countries in Europe had adopted VOC rules that limited the VOC content of certain paint products.1 By 1990 a number of air quality districts, such as SCAQMD (South Coast Air Quality Management District), were regulating Architectural and Industrial Maintenance (AIM) coatings. Additionally, under the 1990 Clean Air Act Amendments (CAAA), the EPA established the Ozone Transport Commission (OTC) to tackle the issue of ozone drifting from one state’s airspace into another’s. And, in 1998, the EPA issued a national rule for VOCs, “National Volatile Organic Compound Emission Standards for Consumer and Commercial Products,” restricting VOC content in most industrial maintenance and marine antifouling coatings to 450 g/L (a limit that is actually above restrictions in some states and districts).2 Lowering VOCs effectively eliminated the use of chlorinated rubbers and vinyls – both of which were extensively used in infrastructure applications. These changing regulations resulted in a technology shift from low-performance systems to high-performance systems, to waterborne systems. Looking back, it is not an exaggeration to say that these technology changes represented a turning point for the industry.

Global Shift Around the same time the protective coatings industry was facing shifting regulations, another shift was occurring that would also have a significant and lasting impact on the industry: the acceleration of infrastructure/economic development beyond the Western world. One such growing market at the time was China, where the economic reform that began in 1978 brought great changes in many areas of Chinese economy, including

By Dr. Karsten Danielmeier, Vice President of Business Development, Coatings, Adhesives & Specialties | Bayer MaterialScience LLC, Pittsburgh, PA APRIL APR IL 2010 | W W W . P C I M A G . C O M

3/16/10 2:42:04 PM

The World Marketplace for Protective Coatings – Opportunities and Trends

40

䡲䡲䡲


2050

2040

2030

2020

2010

2000

1990

1980

1970

1960

1950

Population (billions)

infrastructure development.3 Another growth area was new opportunities, particularly within the context of five Dubai in the United Arab Emirates, which saw economic global megatrends: population growth, globalization/ growth in the 1970s due to revenues from oil and trade. urbanization, climate change/global warming, healthThis growth was further strengthened by the establishcare revolution and accelerated technology changes. ment of Jebel Ali port in 1979, followed by JAFZA (Jebel Population Growth Ali Free Zone), which was built around the port in 1985, As of November 6, 2009, the U.S. Census Bureau estienabling customers to take full advantage of the port’s mated the world’s population to be 6.795 billion.5 While ISO-certified container and general cargo operations.4 Another event that forever changed the global ecothe overall rate of growth is slowing (Figure 1), the nomic landscape was the fall of the Berlin population gains continue to severely tax Wall in 1989. This event, which to many natural resources, making food and water symbolizes the end of the Cold War, was not increasingly scarce. One viable option for only a social revolution, but an economic conserving drinking water is pipeline modrevolution as well, essentially creating new ernization, which minimizes the loss of markets with which the Western world water caused by leakage. This presents could do business. a tremendous opportunity – as well as The significance of this global shift is a challenge – to the protective coatings twofold. First, it created a global market for industry. Additional areas where protechigh-performance coatings products and tive coatings can be utilized to support the technologies needed as these geographic population boom include housing, as well areas built out their infrastructure to help as the construction and repair of the transsupport economic development. Second, it portation infrastructure, among others. also continued the march toward a truly Globalization/Urbanization global economy. This impacted coatings To many, the Burj Al Arab luxury Globalization increases wealth and the manufacturers who needed to ensure their hotel symbolizes Dubai’s urban demand for mobility and communications, products were in compliance with varying transformation. particularly in emerging areas, such as regulations in the different markets. At APAC (Asia and Pacific) and BRICM (Brazil, Russia, India, the same time, it created the opportunity for manufacChina and Mexico). In fact, much has been written about turers to establish facilities in what had until this time how the five BRICM economies will surpass the current been largely untapped markets, translating into improved major economic powers in the decades to come. This is economies of scale, as well as greater manufacturing and a prospect that must be considered for protective coatdistribution efficiencies. ings manufacturers and their suppliers, who may seize Today and Tomorrow: the opportunities these areas offer, and therefore shift Seeds of Change Grow, Blossom the geographic location of their current manufacturing It is with this backdrop of the last 35 years or so in mind operations to be better able to serve these burgeoning that we turn our attention to the protective coatings economies going forward. industry today … and look toward tomorrow. ProductivIn terms of urbanization, significant investments in ity, sustainability and quality are the key drivers in the mass transportation, as well as infrastructure construccoatings industry today. As such, they are both central tion and maintenance, present opportunities for protecand essential to how the industry operates and seizes tive coatings products and technologies, as well. The numbers are, in fact, staggering. A recent report by CIBC World Markets in Toronto predicts that global spending FIGURE 1 | World population: 1950-2050. on infrastructure could reach $25 -$30 trillion over the 10 next two decades. Of this, the United States will account 9 for roughly $150 billion a year in new infrastructure 9 Billion 8 investment; Europe will require roughly $300 billion a 8 Billion year; China, at least $400 billion a year. The report also 7 states that approximately 40 percent of this money will go 6 7 Billion to transport and nearly one-third to power facilities.6 6 Billion 5 Certain countries within such geographic areas 5 Billion 4 as Africa are looking to build new infrastructure to 4 Billion 3 improve not only their economy, but also the health 3 Billion and well being of its people. In an address given Feb. 2, 2 2009, UN Secretary-General Ban Ki-moon stated: “… 1 infrastructural development is key to economic growth 0 and social progress. Africa needs good roads, schools and hospitals; as well as reliable and efficient water services, electricity grids and telecom networks; while Year information and communication technologies must also be a bigger part of Africa’s future. These remain the Source: U.S. Census Bureau, International Data Base, June 2009 Update. APRIL 2010 | W W W . P C I M A G . C O M

3/16/10 2:42:18 PM


building blocks for job creation and the ability to compete in global markets.”7 The United States, on the other hand, is investing significant resources in repairing an infrastructure that is crumbling, or expanding infrastructure that is now inadequate due to population shifts. According to the U.S. Department of Transportation, as of Nov. 3, 2009, nearly 8,500 highway projects have been approved under the American Recovery and Reinvestment Act, and nearly 5,000 highway projects are underway.8

Climate Change/Global Warming From power generation to automotive and nearly everything in between, this megatrend is changing the way companies – and entire industries – do business. Greener solutions that address VOC regulations continue to be an area of focus for the coatings industry. This is particularly true as new and modified regulations are on the horizon. For example, Canada has proposed a 340 g/L limit that is expected to become effective sometime in 2010,

Baseball stadium at Wide World of Sports Disney World in Florida.

and the U.S. EPA is developing an amendment to the national rule that will also be effective in 2010.9 Necessity is the mother of invention, it is said. For the protective coatings industry, the effort to minimize the use of solvents has opened the door to the development and use of more environmentally friendly alternatives, including high-solids coatings, waterborne coatings, waterborne UV coatings and powder coatings. Traditional solventborne polyurethane coatings are typically formulated at a solid level of 30-40 percent, which would

Purity through innovation Global Sieving and Filtration Specialists

Filtration without the Mess or Stress

The Self-Cleaning Russell Eco Filter®... • Improves the quality of your coatings • Tool free & easy disassembly • Reduces your time & labor costs

Call us at: USA: 704 588 9808 Visit ads.pcimag.com 42

䡲䡲䡲


be equivalent to a VOC level of 600 g/L or above. However, the development of lower-viscosity resins, both in the polyol component (polyesters, polyacrylates and polyaspartic esters) as well as low-viscosity polyisocyanates, enables the formulation of high-solids coatings. One approach to the market’s need for higher solids coatings is a new class of co-reactants, namely polyamino coreactants. In the past, the extremely high reactivity of primary amines has prevented their use as a viable co-reactant in coating applications. However, the significantly reduced reactivity of hindered or blocked amines, such as polyaspartic esters and aldimines has allowed for a whole new family of co-reactants available to polyurethane formulators. The coatings based on these polyamino coreactants can be formulated with solid levels in excess of 70 percent, resulting in a system with VOC levels at 2 lbs/ gal or less. The availability of various polyaspartic esters with vastly different reactivities and viscosities makes these compounds more versatile co-reactants for formulators. One can blend two or more polyaspartic esters to achieve a wide range of application viscosities and potlifes. One significant characteristic of the coatings based on polyaspartic esters is that they offer extremely high hardness, balanced with a reasonable flexibility. In addition, both aldimines and polyaspartic esters are compatible with most traditional polyester or polyacrylic resins. The polyaspartic esters can easily be blended with polyesters or polyacrylics to achieve the desired solid level/VOC, hardness, viscosity and cost. For all its advantages, the Journal of Protective Coatings & Linings singled out polyaspartics as one of the top product developments over the last 25 years.10 Successful utilization of this coatings technology was achieved at a baseball stadium at Wide World of Sports Disney World in Florida. An examination of the 125,000-square-foot stadium revealed that a membrane between the structural concrete slab and the topping slab had failed in some areas, allowing water to seep through. Left uncorrected, the leaks could cause damage to the superstructure. To stop the leaks and prevent future water seepage, a team of professionals recommended applying a new external membrane to the concrete topping. The topcoat suggested was a specially formulated color coat based on polyaspartic resins and ali-


3/16/10 2:42:27 PM


phatic isocyanates, which met stringent project requirements that called for a flexible concrete coating with lowto zero-VOCs. This was a smart solution that offered VOC compliance as well as proven long-term durability. And while traditional solventborne polyurethanes have long set the standard for high-performance coatings systems, the development of waterborne polyurethane coatings technologies are offering new, even lower-VOC solutions to the coating formulator. Two-component waterborne polyurethane coatings, when properly formulated with the wide variety of waterborne polyols available, have film characteristics similar to those of solventborne coatings. These properties include high gloss and distinctness of image (DOI), good balance of flexibility and hardness, good abrasion and chemical resistance, and good outdoor weatherability. Much progress continues to be made pertaining to waterborne chemistries. Early waterborne coatings had as much as 300 g/L of co-solvent; new commercial systems are now actually waterborne at 0-15 g/L. A key industry focus is keeping VOCs low while improving product performance. To that end, the industry continues to strive toward the formulation of waterborne coating technologies that can outperform solvent-based coatings in the highest-performing applications. The Los Angeles Unified School District #9 offers another example of the successful implementation of a more eco-friendly coating solution. An anti-graffiti coating system based on 2K waterborne technology was applied to all perimeter poured-in-place concrete walls. In addition to preserving the architect’s desired look of the concrete as a design element, this near zero-VOC coatings solution also met stringent SCAQMD and California Air Resources Board (CARB) guidelines. Often referred to as “dry painting,” powder coatings technology is another option that offers environmental and application advantages. The term “dry painting” refers to powder coatings’ lack of liquid, solvent or water, in its formula. It is applied “dry” directly to a surface in a fine powder form. Because they don’t use

solvents in their formula, powder coatings release little to zero VOCs into the atmosphere. This not only helps the environment, but it also reduces costs for finishers because they no longer have to purchase and maintain expensive pollution control equipment. In addition, most powder coating overspray that does not adhere to the substrate can be reclaimed for future use. As a result, finishers utilize nearly 100 percent of their coating material, leaving little waste and less cleanup. Despite these positive aspects, powder coating has drawbacks, as well: it is less environmentally friendly from an energy consumption perspective and, practically speaking, lacks the durability and weatherability that high-performance applications require.

Healthcare Revolution At first, it may seem unusual to include coatings used in healthcare in a discussion of industrial high-performance coatings. But there are lessons to be learned here. Today, the coatings industry is fine-tuning raw materials up to (semi-)finished materials for the healthcare industry’s product designers, resulting in system solutions. Some examples include topical tissue adhesives, which replace sutures and staples; hydrophilic coatings that facilitate catheter insertion; drug-eluting stent coatings for reduced restenosis and thrombosis, as well as anti-bacterial coatings to minimize the spread of infection. These novel applications remind those of us in the area of high-performance coatings to “think outside the box” when looking ahead to how coatings will be utilized moving forward. In other words, we must rethink the role of coatings and how they will be used differently in the future, presenting new opportunities for functional coatings – such as printed circuit boards and other applications, for example – some of which we may not yet fully understand.

Accelerated Technology Change The evolution of coatings in the healthcare industry segues nicely into the final global megatrend being

CLOSER TO YOU. EVEN IF YOUR WORLD IS TOPSY-TURVY. Regardless of whether you need a quick WACKER solution “down under” or if your desk is “snowed under”: WACKER E-Solutions can help you. You can order products, discuss issues with colleagues and experts worldwide and develop joint solutions – quickly, reliably and highly efficiently. And at the other end of the fast connection, you always know there will be a real person waiting. www.wacker.com/e-business

CREATING TOMORROW‘S SOLUTIONS

038 Bayer FT.indd 44 1 PCI04104WACK.indd

3/16/10 3:17:47 PM 3/8/10 11:42:05 AM

11:42:05 AM

considered for this technical discussion: accelerating technology change. One of the new technologies with implications for a number of industries is nanotechnology. With multi-walled carbon nanotubes (CNTs) it may be possible to combine the best properties of different materials – light metals and polymer compounds – resulting in a new class of materials. As an example, reinforced composite materials based on CNTs and aluminum powder may offer entirely new design opportunities in lightweight construction. CNT-containing components may have much higher mechanical strength, which may mean they can be produced with thinner walls and therefore weigh less than their counterparts of non-reinforced aluminum. The tensile strength of this new class of materials could be similar to that of steel, but weighs only half as much because of its lower density. This weight reduction may result in much improved energy efficiency and a better CO2 balance. For opportunistic protective coatings manufacturers, this may provide an opportunity to formulate new coatings technologies to protect these nano-based structures. Another growing area is coatings based on renewable raw materials, for instance, natural oil-based coatings. Natural oilbased resins, which are used where nature has provided unique structures that are technically and economically viable, may reduce the climate impact of finished products. Applications for these natural oil-based coatings include selfleveling floor coatings, secondary containment and corrosion protection. There is much potential for the protective coatings industry, as owners, architects and engineers increasingly seek out materials that may support LEED certification and its resultant tax credits. Demand for greener technologies is here to stay, and the protective coatings industry must be ready with the appropriate solutions. Functional films is yet another area with exceptionally dynamic growth potential that is pushing the boundaries of the very definition of coatings and the properties they impart to end-use components. This growth includes developments in modern film technologies, holography and polymer electronics. Nanoparticles can play an important role here, for example in electrically conductive printing inks based on nanometallic particles or carbon nanotubes or quantum dots that could be used in the future

in silicon-free organic solar cells – cells that could revolutionize power generation because they could be produced economically in large quantities. Printed light based on coating layers containing electroluminescent pigments within the film and a small source of electricity is another natural transforma-

tion of technology. Near-term applications are primarily for signage and in integral night lighting. But if one looks further into the future, one may envision that these advancements in printed light technology might someday be used to illuminate a wide range of objects in an environmentally responsible way.

Visit ads.pcimag.com PCI06084Shep.indd 1



䡲䡲4/25/08 䡲

2:17:54 45 PM

3/16/10 2:43:12 PM

Shanghai Tiansheng Chemical Co., Ltd.


TIANSORB™ UV Absorbers and Light Stabilizers

Another place to look for inspiration is textiles. The technology behind flexible coatings used to provide abrasion resistance and other desirable properties for soccer balls, for example, could some day be used to formulate coatings that don’t crack or split when being exposed to harsh weather conditions for high-performance applications. Could painting ever be obsolete? Based on current developQuality First - we use medicine standard to produce ments, in the future it may be possible to eliminate the painting our coatings additives. process for bridges or other structures, and instead, wrap it in Good Service - we are committed to provide excellent film, then heat shrink it to fit, resulting in a VOC-free, defect-free service for the customers with our application knowlstructure. This represents a novel process for an organic material edge. and, furthermore, serves to illustrate how the coatings industry must “rethink” the painting process … expanding its definition to Product List (UV Absorbers embrace other innovative ways coatings may be applied. and Light Stabilizers): It sounds incredible, but it’s true. But a look at how far the TIANSORB 1130, TIANSORB 384-2, industry has come in just the last 35 years offers great optimism TIANSORB 99-2, TIANSORB 900, and excitement about the developments that will take place in TIANSORB 123, TIANSORB 292, the next 35 years. Novel chemistries will continue to evolve and TIANSORB 5100, TIANSORB 5151, address new challenges. Considering an integrated perspective TIANSORB 5060, etc. – one that considers global socio-economic factors, as well as For more information, innovative developments in industries as diverse as healthcare, We warmly welcome please contact us at: signage and even sporting goods – creates opportunities for the cross-pollination of ideas, which, in turn, provides fertile ground you to visit us at T: 0086 21 64556108/9/10 in which the next generation’s seeds of change can take root. In ACS Booth # 2909! Email: [email protected] light of the key drivers discussed here – population growth, gloHttp: www.tianshengchem.com.cn balization/ urbanization, climate change/global warming, the healthcare revolution and accelerated technology changes – the Visit ads.pcimag.com protective coatings industry must continue its leadership role in driving innovation forward. For organizations that adopt this pci04104TianQV.indd 1 3/16/10 12:07:40 AM holistic approach, the future will be bright, indeed. 䡲

Shanghai Tiansheng Chemical Co., Ltd. is the professional manufacturer of UV Absorbers and Light Stabilizers in China.Through continuous efforts in R&D, we offer a range of high-quality TIANSORBs to improve the weather resistance of coatings.

GRINDING MEDIA FOR ALL MILLING APPLICATIONS

Any density - any diameter - any composition Zirconium Oxide, Glass, Steel, Steel Shot, Tungsten Carbide, Alumina, Silicon Carbide, Silicon Nitride, Ottawa Sand, Agate, Titanium Oxide, Flint Pebbles, Rare Earth ZrO/CeO, Nickel, Plastics, etc. Precision Glass Balls for ball bearings, check valves, level gauges and low temperature critical applications are also available Small orders welcome. www.glenmills.com

Large stocks - Competitive Prices - Attentive service. Please phone for full information and prices.

References Dankin, M. Spanning 25 Years of Development in Heavy-Duty Coatings. J. of Protective Coatings and Linings 2009, 8, 47. 2 Kaelin, A. B.; Kapsanis, K. A. Regulations and Coatings Work: Developments Over 25 Years. J. of Protective Coatings and Linings 2009, 8, 73-74. 3 Public Infrastructure Development in China. Lin, Shuanglin Comparative Economic Studies, June 22, 2001. 4 UAEFreeZones.com. 5 U.S. Census Bureau – International Database. 6 Benjamin Tal, “Capitalizing on the Upcoming Infrastructure Stimulus,” CIBC World Markets, Jan. 26, 2009. 7 “Development of Africa’s Infrastructure Key to Economic Growth, Social Progress,” United Nations new release, Feb. 2, 2009. 8 “Highway Investment Hits $20 Billion,” U.S. Department of Transportation, Nov. 3, 2009. 9 Harding, M. Update on Low VOC Regulations for Coatings. J. of Protective Coatings and Linings 2009, 10, 23. 10 Hower, H. Top Product Developments, 1984 to the Present. J. of Protective Coatings and Linings 2009, 8, 67-68. 1

This paper was presented at PACE 2010, Phoenix, AZ. For more information, visit www.pace2010.com, www.bayermaterialscience.com and www.bayermaterialsciencenafta.com.

Go to www.pcimag.com/fbfan

Glen Mills Inc. 220 Delawanna Ave., Clifton, NJ 07014 Tel: (973) 777-0777 Fax: (973) 777-0070 Visit ads.pcimag.com 46

䡲䡲䡲



3/16/10 3:19:07 PM

The Use of

Mixed Metal Oxide Pigments

M

in Industrial Coatings

ixed metal oxide (MMO) pigments, also known as complex inorganic color pigments (CICPs), have been around since the early 1800s. Their use in the ceramic and pottery industries is well known due to their overall inertness, which contributes to outstanding heat, chemical and UV resistance. The use of MMOs in industrial coatings is less common and more for special purposes. This paper will discuss the benefits of formulating coatings with MMOs as a replacement for, or in conjunction with, the more common organic types. Mixed metal oxide pigments are compounds comprised of a group of two or more metals and oxygen. The most common crystal structures are rutile (MeO2) hematite (Me2O3) or spinel (Me3O4). Metals commonly present include: cobalt, iron, trivalent chrome, tin, antimony, titanium, manganese and

aluminum. Different metal combinations produce a wide spectrum of hues ranging from black to brown to green, blue, yellow and red. All MMOs are produced by a calcination process consisting of an intimate mixture of appropriate metal precursor materials being fired at temperatures of 800 to 1300 °C. It is this calcining process that creates the extremely stable metal oxide bonds. The chemical stability of these bonds affords the outstanding durability of this class of color pigments.

UV Durability The chemical inertness of inorganic MMOs renders their excellent resistance to UV radiation and the elements encountered in the most extreme outdoor environments. Most organic pigments degrade when exposed for more than a few years in UV-intense tropical environments. High-performance organic pigments that do provide acceptable durability

Common Mixed Metal Oxide Pigments

C.I. Name

Chemistry

CAS #

Name

Structure

Color

PBrn 33

(Zn,Fe(Fe,Cr)2O4

68186-88-9

Zinc iron chromite

Spinel

Reddish brown

PBrn 35

Fe2CrO4

68187-09-7

Iron chromite

Spinel

Dark brown

PY 53

(Ni Ti Sb)O2

8007-18-9

Nickel antimony titanate

Rutile

Yellow Yellow tan

PBr 24

(Ti, Cr, Sb)O2

68186-90-3

Chrome antimony titanium buff

Rutile

PG 17

CrOAl

68909-79-5

Chromium green

Hematite

Yellowish green

PG 26

CoCr2O4

68187-49-5

Cobalt chromite

Spinel

Green

PG 50

Co2TiO4

68186-85-6

Cobalt titanate

Rutile

Green

PG 17 Blk

CrOFe

68909-79-5

Chromium green-black

Hematite

Brownish black

PBlk 28

CuCr2O4

68186-91-4

Copper chromite black

Spinel

Black

PBlk 30

(Ni,Fe)(Cr,Fe)2O4

71631-15-7

Chrome iron nickel black

Spinel

Black

PB 28

CoAl2O4

1345-16-0

Cobalt aluminate

Spinel

Reddish blue

PB 36

Co(Al,Cr)2O4

68187-11-1

Cobalt chromium aluminate

Spinel

Turquois

PY 119

(Zn Fe)Fe2O4

68187-51-9

Zinc ferrite

Spinel

Brown

By Kevin Biller | Mason Color Pigments, East Liverpool, OH 48

䡲䡲䡲

048 Biller FT.indd 48


3/16/10 2:40:07 PM

are typically very expensive, commanding two to four times the cost of a metal oxide pigment. MMOs are therefore the colorant material of choice for architectural coatings requiring extremely high durability such as the performance specified in AAMA 2605-05 (Architectural Aluminum Manufacturers Association). This specification calls for maintenance of color and gloss after 10 years exposure in south Florida.

Chemical Resistance The exceptionally stable chemical bonds characteristic of MMO pigments make them insoluble in most chemicals including strong acid and alkali, and virtually all organic solvents. Because of this insolubility, coatings formulated with MMOs will not lose color due to pigment degradation even with the most extreme exposure to aggressive chemicals. Atmospheric pollution including acid rain, volcanic fallout and waste incineration does not chemically attack these pigments. Moreover, coatings requiring resistance to strong chemical exposure such as laboratory and chemical manufacturing facilities can use MMOs and be assured of color stability.

Heat Resistance The thermal stability of MMOs is well known in the ceramic and pottery industries. This class of pigments is processed for hours at temperatures ranging from 800 to 1300 °C in their manufacture. Consequently, they are chemically and color stable at these temperatures in service. As mentioned, the ceramic industry has used mixed metal oxides for color glazes for centuries. The glazes used in ceramics are regularly fired at temperatures of 985 to 1300 °C (1800 to 2350 °F) without significant color shift. The use of MMOs in thermally stable coating formulations such as those based on silicone (polysiloxane) resins brings a palette superseding the traditional black and silver high-heat choices. This brings an attractive array of color possibilities to the designer of specialized and sport transportation such as motorcycles, ATVs and jet skis.

Infrared Reflectivity Metal oxide pigments possess unique spectroscopic properties. The infrared reflective characteristics of the cobalt chromite, cobalt titanate and chrome oxide greens make them ideal for non-detectable camouflage coatings. Common organic green pigments such as those based on copper phthalocyanine strongly absorb infrared radiation and make them a poor choice for military coatings.

region, causing a significant increase in surface temperature. This increased temperature is deleterious for a number of reasons. Most important are coatings used for architectural structures such as roofing and cladding. The heat increase associated with highly absorptive organic pigments causes the temperature of the interior of buildings to rise. This obviously translates into higher cooling costs in summer months. MMOs provide substantially higher infrared reflectivity (total solar reflectivity – TSR) and therefore stay cooler in the sunlight. The Lawrence Berkeley National Laboratory has conducted extensive research and has qualified a large amount of MMOs as replacements for poorly reflective organic pigments (http://coolcolors.lbl. gov/LBNL-Pigment-Database/database.html). IR reflective pigmentation has other practical uses. Maintaining cooler surfaces of playground equipment, park benches, outdoor sports facilities and bus stops provides more comfort and a safer surface in sunny locales. Furthermore, cooler surfaces on utility cabinetry such as cable junction boxes, electrical enclosures and outdoor generators keeps internal components cooler and increases product longevity and minimizes service calls. Mixed Metal Oxide Crystal Morphology

Crystal Type

Chemistry

Rutile

MeO2

Hematite

Me2O3

Spinel

Me3O4

Crystal Structure

Solar Reflectivity One of the more exciting developments in MMO technology is the recognition of how this pigment technology can provide colors that significantly reflect the infrared energy generated by the sun. Colored materials, including pigments and dyes, absorb and reflect radiation in the visible range (approximately 400 to 700 nm). They also inherently reflect and absorb in the near-infrared region (700 to 2500 nm) of radiation. It is this range that is responsible for the increase of temperature experienced when colored surfaces are exposed to sunlight. Organic pigments, especially carbon black and phthalocyanine types (blue and green), absorb strongly in this

Me = metal atom PA I N T & C O A T I N G S I N D U S T R Y


䡲䡲䡲

49

3/16/10 2:40:16 PM

The Use of Mixed Metal Oxide Pigments in Industrial Coatings

Cooler coating temperatures not only provide comfort and increased component longevity but also improve the overall durability of the coating system. The lower temperatures experienced in service keep the coating binder cooler and thus slow the chemical degradation of the polymers in the coating. Highest reflectivity is characteristic of yellows (PY 53 and PBrn 24), browns (PBrn 33 and PBrn 35), some greens (PG 17) and some blacks (PG 17 and PBrn 35). Blues (PB 28 and PB 36) and greens (PG 17, PG 26 and PG 50) provide reasonable alternatives to traditional organic types.

for an architectural or automotive coating while maintaining or improving durability. In some cases an improvement in hiding can be realized.

Organic Pigment Extenders

Summary

Mixed metal oxides can enhance the durability and lower the cost of coatings formulated with high-performance organic pigment systems. This is especially relevant in bright yellow, orange and red color spaces. These organic hues not only are relatively weak in hiding (opacifying) properties, they typically possess high oil absorption, which affect rheological properties especially at the high concentrations needed to achieve acceptable opacity. MMOs have relatively low oil absorption compared to their organic counterparts, thus providing improved flow and leveling in industrial coatings. This is especially true in powder coatings, which rely on resin melt viscosity to achieve a smooth finish. The incorporation of pigment yellow 53 or pigment brown 24 (yellow buff) typically lowers the overall cost of pigmentation

Mixed metal oxide pigment technology is well known and timetested in the decorative ceramics industry. Its widespread use in organic coatings has not yet reached its full potential. These pigments offer a multitude of benefits for the coatings formulator, including excellent outdoor durability, chemical resistance and heat stability. Inherent infrared reflective properties make them a good foundation for camouflage and “cool” coatings. The low oil absorption characteristic of MMOs allow them to reduce the concentration of high-cost, high-performance organic pigments with a positive effect on coating rheology. The coatings formulator is therefore strongly encouraged to include this class of pigments in his or her formulating toolkit. 䡲

Tinting in Pastels In general MMOs are weaker and somewhat lower in tint strength compared to organic pigments. Because of this, they are an excellent choice to tint white and pastel colors. This is especially true when compared to difficult-to-disperse organic pigments such as phthalocyanine blues and greens and carbon black.

For more information, visit www.masoncolorpigments.com.

See it in action at www.hockmeyer.com/videos/HCPS Think your product is for an Immersion Mill?

THINK AGAIN!

Equipment Corporation Proudly introduces the New HCPS Immersion Mill Design featuring the addition of an upper auger and g p blades interchangeable scraper idewall Scrap Ancho Sidewall Scraper Anchor Helix blade The “S” series is designed for proce processing high /or highly thixotropic products viscosity and/or www.hockmeyer.com

(252) 338-4705

up to 400,000 cps!

[email protected]

TESTING AVAILABLE!

Visit ads.pcimag.com PCI10084Hock.indd 1

50

䡲䡲䡲


7/1/08 1:27:14 PM


3/16/10 2:40:25 PM

Novel, Environmentally Friendly Corrosion Inhibitor for

Self-Etching Wash Primers

T

his study found that an etch-primer formulation that incorporated Nubirox 301 showed comparable results in adhesion and corrosion inhibition when compared to a traditional, commercial etch primer that contained zinc tetraoxy chromate. Nubirox 301, a calcium and strontium phosphosilicate corrosion inhibitor, gives an effective and cost-efficient pathway to making an environmentally friendly self-etching primer. The formulations were applied to three different substrates (cold rolled steel, galvanized steel and aluminum) and were put through a series of tests (EIS, SEM/EDX Analysis, ASTM B 117, ASTM D 5894 and ASTM D 4585). Each of the tests concluded that, overall, the addition of Nubirox 301 showed the most advantageous results. The formulations were in compliance with low-VOC requirements; however, since the commercial etch primer contained the zinc tetraoxy chromate, it still required the reporting of that environmentally hazardous substance. Nubirox 301,

FIGURE 1 | EIS test model. Electrolyte

Reference Electrode

Coating

Corrosion Reaction

Coating Capacitance (Coating)

Uncompensated Pore Resistance Resistance (Ru) (Rpore)

Metal

Working Electrode Double Layer Capacitance (Cdl) Polarization Resistance (Rp)

however, is not only chrome-free, it is zinc-free as well – therefore, it is not required to report this inhibitor for environmental compliance.

Introduction In the automobile refinishing and industrial manufacturing industries, and where untreated or bare metal is painted, an etch primer is typically used to increase adhesion of the paint to the metal surface and to improve the anticorrosive quality of the coating. Historically, etch primers have utilized zinc tetraoxy chromate as the primary corrosion inhibitor. However due to the toxicity and carcinogenic concerns associated with chromates, as well as the dawning of the new era of “green regulations”, an environmentally friendly alternative is needed for this market. Zinc phosphate corrosion inhibitors have been studied as a replacement for zinc tetraoxy chromate in this type of application, and they have seen limited success. Historically, zinc phosphate has exhibited similar performance to chromates in real-world outside exposure. However, in harsher conditions such as marine environments and accelerated salt spray or prohesion testing, the results are less favorable; however, it is important to note that under these more harsh conditions, zinc phosphate still helps in the preservation of the metal substrate, just not to the degree the chromate presents. Even though zinc is not considered a heavy metal, it is still a requirement to report its use. Etch primers are traditionally formulated with phosphoric acid and zinc tetraoxy chromate in an alcohol medium, using polyvinyl butyral as the binder, which acts as a ligand of the reaction products. As new global environmental standards are put in place, stricter formulation guidelines will become prevalent. In the near future a push

By Rebecca R. Daley and Dr. Steve A. Hodges, Nubiola Inorganic Pigments | Nubiola USA, Norcross, GA 52

䡲䡲䡲

052 Nubiola FT.indd 52


3/16/10 4:31:32 PM

Project Design The formulations were based on an epoxy/phenolic-modified polyvinyl butyral (PVB) system. The pigment volume concentration (PVC) of each formulation was held constant at 12%, and the PVC/CPVC ratio remained at 0.29. Four Nubirox inhibitors, and combinations thereof, were evaluated at different levels in order to determine which gave the most advantageous results. In all, there were 10 experimental data points evaluated, along with two controls (a commercially available zinc tetraoxy chromate-containing (5.5% by total formula weight) selfetching wash primer along with one that is chrome-free and utilizes zinc phosphate (5% by total formula weight)). The four Nubirox inhibitors evaluated were: • Nubirox N2 – standard zinc phosphate; • Nubirox 106 –molybdate-modified zinc phosphate; • Nubirox 213 – multiphase iron and zinc phosphate; and • Nubirox 301 – calcium and strontium phosphosilicate; along with a 1:1 ratio of combinations of the following inhibitors: • Nubirox 213 : Nubirox 106; • Nubirox 213 : Nubirox 301; and • Nubirox 106 : Nubirox 301. The inhibitors were evaluated at two loading levels, 1.5% total formula weight (t.f.w.) and 3.0% t.f.w. – with the exception of the Nubirox N2, which was only evaluated at 1.5% t.f.w. Each combination of inhibitors was evaluated at the loading of 1.5% t.f.w. per inhibitor. The formulations were evaluated over three types of substrates – galvanized steel, cold rolled steel and aluminum. A total of 432 panels were coated via spray application using a HVLP (high-volume low-pressure) spray gun. The top half of each panel showed the self-etching primer alone, and the lower half showed the etch primer along with a commercially available intermediate sanding primer. One panel for each test was also sprayed with a commercially available acrylic topcoat. Characterization of the film formed by the etch-primer formulations was done via Electro-Impedance Spectroscopy (EIS, see Figure 1) and SEM/EDX analysis. The panels were allowed to rest for 7 days before corrosion testing began. They were then evaluated to assess blistering, rusting and adhesion via accelerated ASTM D 4585 humidity testing, ASTM B-117 salt spray testing, as well as ASTM D 5894 cyclic QUV/prohesion testing.

FIGURE 2 | EIS values from the highest performance formulations. 109 100

acdcac: -2 V, 20 min, 25 min EIS, 3h relax

107

60

105

40 103 101 10-4

Phase Θ (*)

80

20 10-2

100 102 Frequency (Hz)

104

0 106

FIGURE 3 | SEM/EDX mapping. Exp. 7

Exp. 6

Exp. 5

Exp. 4

Exp. 3

Exp.

Exp. 2

Control

TABLE 1 | Aluminum salt spray evaluation. Aluminum Visual Rating TEST TYPE: ASTM B 117 Hrs in Test: 309 % Addition (t.f.w.)

Inhibitor

Blister

Scribe Rust

Field Rust

5% 5.5% 3% 1.5% 3%

Zinc phosphate Zinc tetraoxy chromate Nubirox 213 Nubirox 106 Nubirox 301

D4 None MD2 M2 None

10 10 10 10 10

10 10 10 10 10

TABLE 2 | Aluminum Prohesion evaluation. Aluminum Visual Rating TEST TYPE: ASTM D 5894 % Addition Inhibitor (t.f.w.) 5% 5.5% 3% 1.5% 3%


Hrs in Test: 537 Blister

Scribe Rust

Field Rust

MD4 None MD4 D2 None

10 10 10 10 10

10 10 10 10 10



Exp. 1 Exp. 2 Control Exp. 3 Exp. 4

Biode Diagram

|Z| Ω

to lower VOCs and HAPS-free systems, to eliminate chrome, to limit reportable compounds, and to develop water-based hybrids are in store for the etch-primer market. The objective of the work presented herein was to develop a chrome-free self-etching primer that meets current and future global environmental demands, as well as offer improved performance over an existing chrome-free formula utilizing zinc phosphate and comparable to improved results to an industry-standard zinc tetraoxy chromate-containing etch primer. A range of Nubirox corrosion inhibitors were evaluated in this study in order to determine which chrome-free inhibitor showed the best results.

䡲䡲䡲

53

3/16/10 4:31:41 PM

Novel, Environmentally Friendly Corrosion Inhibitor for Self-Etching Wash Primers

FIGURE 4 | Salt spray pictorial results.

FIGURE 5 | Cyclic QUV/prohesion pictorial results.

2K PVB Etch / Wash Primer C.R.S. / D.F.T ~ 0.7 Mils (top) ~3 Mils (bottom) / 309 hours Salt Spray Testing (ASTM B117)

FIGURE 6 | Additional testing using a different 2K self-etching wash primer.

2K PVB Etch / Wash Primer C.R.S. / D.F.T ~ 0.7 Mils (top) ~3 Mils (bottom) / 537 hours QUV/Probation Testing (ASTM D5834)

2K PVB Etch / Wash Primer C.R.S. / D.F.T ~ 0.8 Mils 301hours Salt Spray Testing (ASTM B117)

Control 1 5.0% Zinc Phosphate

Control 2 3.0% 1.5% 3.0% 5.5% Zinc Nubirox 213 Nubirox 106 Nubirox 301 Tetraoxy Chromate Percentages based on total formula weight

Figure 4 (a): Cold Rolled Steel



Figure 5 (a): Cold Rolled Steel 5.5% Lf.w Zinc Tetraoxy Chromate

2K PVB Etch / Wash Primer

2K PVB Etch / Wash Primer

Aluminum / D.F.T ~ 0.7 Mils (top) ~3 Mils (bottom) / 309 hours Salt Spray Testing (ASTM B117)

Aluminum / D.F.T ~ 0.7 Mils (top) ~3 Mils (bottom) / 537 hours QUV/Probation Testing (ASTM D5834

1.5% Lf.w Nubriox 301



Figure 6 (a): ASTM B 117 (Cold Rolled Steel) 2K PVB Etch / Wash Primer C.R.S. / D.F.T ~ 0.8 Mils /504 hours Cyclic QUV/Probation Testing(ASTM D5894)





Figure 5 (b): Aluminum

Figure 4 (b): Aluminum

2K PVB Etch / Wash Primer 2K PVB Etch / Wash Primer

Galvanized Steel / D.F.T ~ 0.7 Mils (top) ~3 Mils (bottom) / 537 hours QUV/Probation Testing (ASTM D5834)

Galvanized Steel / D.F.T ~ 0.7 Mils (top) ~3 Mils (bottom) / 309 hours Salt Spray Testing (ASTM B117

5.5% Lf.w Zinc Tetraoxy Chromate




Figure 6 (b): ASTM D 5894 (Cold Rolled Steel) 2K PVB Etch / Wash Primer Galvanized Steel / D.F.T ~ 0.8 Mils /301 hours Salt Spray Testing (ASTM B117)



Figure 4 (c): Galvanized Steel Each test contained three replicates of each experimental and of each control – one topcoat along with two etch/etchintermediate panels. The ASTM D 4585 humidity testing was conducted for a set 94 hours; however, in the other tests the panels were periodically evaluated and when enough differential was seen among all the experiments as well as the controls, the panels were removed from test, the middle portion of the film was stripped, and the metal beneath the film was then evaluated via ASTM D 610 for panel corrosion, ASTM D 1654 for scribe corrosion and ASTM D 714 for panel/scribe blister.

Results The EIS values from the highest performance formulations can be seen in Figure 54

䡲䡲䡲




Figure 5 (c): Galvanized Steel 2. As can be seen, Nubirox 301 at 3% by t.f.w. (shown as Exp 2 denoted by red circles) exhibited similar trend in impedance values as that of zinc tetraoxy chromate (shown as control denoted by green triangles). The remaining experiments denoted on the chart are as follows: Exp. 1 Nubirox 106 at 1.5% by t.f.w., Exp. 3 Nubirox 213 at 3% by t.f.w., and Exp. 4 Nubirox N2 at 1.5% by t.f.w. SEM-EDX is the name of the energydispersive X-ray spectroscopy analysis conducted by means of scanning electron microscopy. It is an analytical technique used to determine the chemical composition of a given specimen as well as its morphology and structure. SEM-EDX analysis was employed in this study for mapping quantitative and qualitative oxidation generation on the surface of the various substrates.






Figure 6 (c): ASTM B 117 (Galvanized Steel) 2K PVB Etch / Wash Primer Galvanized Steel / D.F.T ~ 0.8 Mils /504 Cyclic QUV/Probation Testing(ASTM D5894)






Figure 6 (d): ASTM D 5894 (Galvanized Steel)


3/16/10 4:31:48 PM


TABLE 3 | Cold rolled steel salt spray evaluation. Cold Rolled Steel Visual Rating TEST TYPE: ASTM B 117 Hrs in Test: 309 % Addition Inhibitor Blister Scribe Rust (t.f.w.) 5% 5.5% 3% 1.5% 3%


None None D2 M4 M2

Field Rust

7 5 8 8 6

3 2 3 6 4

TABLE 4 | Cold rolled steel Prohesion evaluation. Cold Rolled Steel Visual Rating TEST TYPE: ASTM D 5894 Hrs in Test: 537 % Addition (t.f.w.)

Inhibitor

Blister

Scribe Rust

Field Rust

5% 5.5% 3% 1.5% 3%


None F2 MD4 F4 None

7 9 7 7 10

2 10 3 6 10

TABLE 5 | Galvanized steel salt spray evaluation. Galvanized Steel Visual Rating TEST TYPE: ASTM B 117 Hrs in Test: 309 % Addition (t.f.w.)

Inhibitor

Blister

Scribe Rust

Field Rust

5% 5.5% 3% 1.5% 3%


F2 None None None None

10 10 10 10 10

8 9 8 7 10

TABLE 6 | Galvanized steel Prohesion evaluation. Galvanized Steel Visual Rating TEST TYPE: ASTM D 5894 Hrs in Test: 537 % Addition Inhibitor Blister Scribe Rust Field Rust (t.f.w.) 5% 5.5% 3% 1.5% 3%


MD4 None F4 D3 None

9 10 10 9 10

8 10 7 7 10

FIGURE 7 | Paint film depiction of phosphoric acid reaction to form the passive layer. Paint Film Ca+2

Sr+2

Sr+2

Ca+2

Ca+2

Sr+2 H3PO4 -

H3PO4 -

Passive Layer (CaO · SrO · P2O5 ) Substrate

[Ca2SiO4·3SrCO3 + 2H3PO4 + XH2O → 2CaO·Sr3(PO4)2·SiO2 + XH2O + 3CO2↑] 56

䡲䡲䡲


The pictorial results from the SEM/EDX analysis are shown below in Figure 3. As with the EIS values, the results from this analysis show that the Nubirox 301 at 3% by t.f.w. is most comparable to the 5.5% by t.f.w. zinc tetraoxy chromate. Exp. 1-4 shown are the same from the EIS evaluation; Exp 5-7 are the 1:1 blends. In accelerated corrosion testing, overall the best results were seen with the addition of Nubirox 301 at 3.0% t.f.w. Nubirox 301, in both salt spray and prohesion tests and on all substrates, showed better adhesion promotion, less field corrosion, and comparable to improved scribe rust inhibition in comparison to the control utilizing 5% by t.f.w. standard zinc phosphate. Nubirox 301 at 3.0% t.f.w. also had comparable to improved results to the etch primer containing 5.5% by t.f.w. zinc tetraoxy chromate (Figures 4 and 5). The salt spray (ASTM B 117) testing was pulled after 309 hours, and the cyclic QUV/prohesion (ASTM D 5894) testing was pulled after 537 hours. Additional testing was conducted using a slightly different 2K self-etching wash primer. These results (Figure 6) also show Nubirox 301 having advantageous results when compared to zinc tetraoxy chromate in both the ASTM B 117 and the ASTM D 5894 testing on cold rolled and galvanized steel. These additional pictorial results show the etch primer alone – with no intermediate primer. As stated previously, each panel was rated via ASTM D 610 for panel corrosion, ASTM D 1654 for scribe corrosion, and ASTM D 714 for panel/scribe blister. Tables 1 through 6 give the detailed ratings of the experiments that exhibited the best results (correlating pictorial results from Figures 4 and 5). The blister ratings are as follows: F (for few), M (for medium), MD (for medium dense) and D (for dense) – along with a number to designate the percent of area affected. The field rust rating ranges from 10 (being no area affected) to 0 (being over 50 percent rusted). The scribe rust rating ranges from 10 (being no rust from scribe) to 0 (being over 16 mm rust from scribe). Each of these rating scales is directly taken from the respective ASTM.

Summary It is apparent by both the pictorial results and the ASTM evaluations that Nubirox 301 presents a favorable alternative to chrome in a 2K epoxy/phenolic PVB etch primer system. The results show that Nubirox 301 shows overall comparable results to zinc chromate in this system, and in most cases out-performs standard zinc phosphate, which is the current alternative. Nubirox 301, an “eco-friendly” zinc-free corrosion inhibitor, meets both the ever increasing and limiting environmental demands, as well as the performance requirements needed for this type of application. Nubirox 301 is a calcium and strontium phosphate complex carried on a silicate core. The calcium and strontium cations provide direct anodic inhibition, where the silica-core alkalinity provides good cathodic inhibition. This chemical composition works within the etch-primer formulation and reacts with the phosphoric acid to form the passive layer seen in Figure 7. In addition to the chemical activity of this corrosion inhibitor, Nubirox 301 has a unique particle morphol-


3/16/10 4:31:58 PM


ogy, a fine mean particle size, along with a narrow particle size distribution (Figure 8) – thus providing more uniform pigment packing, which allows for excellent thin-film performance. This is ideal for the etch primer market, seeing that the primer is typically applied at less than 1 mil (25 µ) dry film thickness. It also lends to the excellent package stability found with Nubirox 301 in this system.

FIGURE 8 | SEM and Malvern sedigraph of Nubirox 301. 500μ

Conclusions

Nubirox 301 Particle Size Distribution (Malvern Sedigraph) 50%

0.01

0.1

100% 90 80 70 60 50 40 30 20 10 0

1.0 10.0 100.0 Particle Diameter (μm.) Avg. Particle Size = 1.0 μ

1000.0

• Nubirox 301 at an addition of 3.0% t.f.w. in a 2K epoxy/phenolic-modified PVB self-etching wash primer showed comparable results vs. a commercially available zinc tetraoxy chromatecontaining etch primer. • Nubirox 301 (zinc-free) was the most effective non-chrome inhibitor for multi-substrates. • Nubirox 301 is a calcium and strontium phosphate complex carried on a silicate core; therefore, it is not only chrome-free, it is zinc-free as well. Thus it is the most eco-friendly alternative available. There are no components of this inhibitor that are required to be reported. • The fine particle size of Nubirox 301 is ideal for thin film systems such as etch primers. 䡲

Acknowledgements

• Nathan Karszes, Laboratory Manager, Nubiola North American Technology Center. • Richard March Raurell, R&D Manager, Nubiola Spain.

Trying to solubilize your resin in an exempt solvent ? 100 Parts OXSOL® 100 100 Parts K-FLEX® 188

50 Parts OXSOL® 100 100 Parts POLYESTER A

45 Parts OXSOL® 100 100 Parts POLYESTER B

100 Parts OXSOL® 100 100 Parts K-FLEX® A308

Viscosity Reduction Curves - With K-FLEX® A308 1800 1600 1400 1200 1000 800 600 400 200 0

We’ve got an ADD for that ! K-FLEX® 188 and A308 polyester polyols are not only soluble in a variety of exempt solvents but can be used to solubilize other resins offering: x x x x

1

2

3

4

A ceto ne

TB A

% So lvent

Oxso l® 100

Improved film properties Improved compatibility of most resins in exempt solvents Reduced viscosity Reduced VOC’s

To find the perfect ADD for your APP...Visit: www.kingindustries.com

Oxsol® is a registered trademark of Makhteshim-Agan of North America Inc.

K-FLEX® 188 & A308 Resin Modifiers Attend “New Tin Free Organometallic Catalysts for Urethanes” ACS Conference - 11:30 AM - April 14 - Session 15.5

or King Industries - Booth #2515 at the American Coatings Show Science Road Norwalk, CT 06852 (203) 866-5551 [email protected]


䡲䡲䡲



3/16/10 4:32:08 PM

Paint Formulations and the Need for Zeta Potential As latex waterborne paints command a growing share of the market, zeta potential measurement and its manipulation is increasingly important for product optimization.

P

aints are multi-component systems formulated to produce specific product properties. The rate and uniformity at which these coatings wet spread and coalesce into a film can be controlled by the constituents in the formulation. Depending on their end use, coatings can have four or more components in their mixture. Solid or higher-viscosity components consist of pigments used to obtain a specific color, and oil emulsions or latex components that provide film formation or coating properties. Both are mixed with a number of water-soluble materials, such as surfactants, silanes, viscosity modifiers, processing aids, color aids and polyelectrolytes, which can also be surface active. These water-soluble surface-active elements can affect the surface chemistry or interfacial behavior of the solid particle components. The soluble components play a vital role in the final film properties and color of a paint formulation, and can be studied using zeta potential. Zeta potential is a physical property exhibited by any particle in suspension. It can be quantified using elec-

Zetasizer Nano

trophoretic mobility (electrophoresis) measurement and adjusted to optimize coating formulations. Studying zeta potential results enables the building of relationships between the chemical composition of formulated coatings and the required final physical properties and color. Today, zeta potential is easy to measure and aids in predicting long-term stability and optimizing product properties.

Electrophoresis When an electric field is applied across an electrolyte, suspended charged particles are attracted to the electrode of opposite charge. Viscous forces acting on the particles tend to oppose this movement. When equilibrium is reached between the two opposing forces, the particles move with constant velocity. This velocity depends on electric field or voltage gradient strength, the dielectric constant of the medium, its viscosity and the zeta potential. A particle’s velocity in a unit electric field is known as its electrophoretic mobility. Zeta potential is related to electrophoretic mobility through the Henry equation, which relates it to zeta potential based on physical constants such

By Ana Morfesis | Malvern Instruments Inc., Westborough, MA 60

䡲䡲䡲

060 Malvern FT.indd 60


3/16/10 2:38:20 PM

as the dielectric constant, viscosity and ionic strength of the medium. Current instrumentation makes zeta potential measurement easy and automatic.

Measuring Electrophoretic Mobility The essence of a classical micro-electrophoresis system is a capillary cell with electrodes at either end, to which a potential is applied. Particles move towards the electrode, their velocity is measured and is expressed in unit field strength as their mobility. Early methods involved direct observation of individual particles using ultra-microscope techniques. This procedure suffers from a number of disadvantages, including the strenuous effort required to make a measurement, particularly with small or poorly scattering particles. Modern methods, however, are fully automated. One of the most widely used systems is the Zetasizer Nano (Malvern Instruments), which combines laser Doppler electrophoresis with phase analysis light scattering (PALS) in the patented M3-PALS technique. This allows measurement of particle electrophoretic mobility even in samples with low mobility and also in high-conductivity samples. In addition, the low voltages involved avoid any risk of sample effects due to heating.

• Electrostatic or charge stabilization is the effect on particle interaction due to the distribution of charged species in the system. Each mechanism has its benefits for particular systems. Steric stabilization is simple, requiring only a suitable polymer. However, it can be difficult subsequently to flocculate the system if this is what is required. Expense may be a drawback, and sometimes it is not desirable to have a polymer present. Electrostatic or charge stabilization works by simply altering the concentration of ions in the system – a reversible and potentially inexpensive process. Zeta potential has long been recognized as a very good index of the magnitude of the interaction between colloi-

FIGURE 1 | Optical configuration of the Zetasizer Nano series for zeta potential measurements. 6

7

Combining optics

Compensation Scattering optics beam

Beam splitter Incident beam

Attenuator Cell

Optical Configuration Laser

tec

tor

1 De

A zeta potential measurement system consists of six main components (Figure 1). First, a laser [1] is used as a light source to illuminate the particles within the sample. For zeta potential measurements, this is split to provide an incident and reference beam. The incident beam passes through the center of the sample cell [2], and the light scattered at a forward angle is detected [3]. When an electric field is applied across the cell, any particles moving through the measurement volume will cause the intensity of light detected to fluctuate with a frequency proportional to the particle speed, and this information is passed to a digital signal processor [4] and onto a computer [5]. The Zetasizer Nano software, for example, produces a frequency spectrum from which the electrophoretic mobility and hence zeta potential information is calculated. The intensity of the detected, scattered light must be within a specific range for the detector to successfully measure it. This is achieved using an attenuator [6], which reduces the intensity of the laser and, hence, reduces the intensity of the scattering. To correct for any differences in the cell wall thickness and dispersant refraction, compensation optics [7] are installed to maintain optimum alignment.

2

Reference beam

Digital signal processor

5

4

3

FIGURE 2 | Steric and electrostatic stabilization mechanisms of colloidal dispersions.

Stability and Interfacial Surface Effects Two fundamental mechanisms affect dispersion stability (Figure 2). • Steric repulsion – where polymers added to the system adsorb onto the particle surface and preventing particle surfaces coming into close contact. When sufficient polymer adsorbs, the thickness of the coating is enough to maintain particle separation through steric repulsion between the polymer layers. At such separations the van der Waals forces are too weak to cause the particles to adhere.

Steric stabilization

Electrostatic stabilization



䡲䡲䡲

61

3/16/10 2:38:28 PM

Paint Formulations and the Need for Zeta Potential

FIGURE 3 | Schematic representation of zeta potential. Electrical double layer Stern layer

Diffuse layer

from the surface, the surface would be uncharged. In fact silver ions dissolve preferentially, leaving a negatively charged surface. If Ag+ ions are now added the charge falls to zero. Further addition leads to a positively charged surface.

Adsorption of Charged Species (Ions and Ionic Surfactants) Surfactant ions may be specifically adsorbed on the surface of a particle, leading, in the case of cationic surfactants, to a positively charged surface and, in the case of anionic surfactants, to a negatively charged surface.

The Electrical Double Layer Negatively charged particle

Slipping plane

Based on the above mechanisms, latexes, pigments and in fact most materials suspended in aqueous media, carry a surface charge. The development of a net charge at the particle surface affects the distribution of ions in the surrounding interfacial region, resulting in an increased concentration of counter ions (ions of opposite charge to that of the particle) close to the surface. Thus an electrical double layer exists round each particle.

Zeta Potential

Surface potential Zeta potential

mV

Distance from particle surface dal particles. Zeta potential measurements are commonly used to assess the stability of colloidal systems.

Origins of Surface Charge Most colloidal dispersions in aqueous media carry an electric charge. This can originate in many ways depending upon the nature of the particle and its surrounding medium. The more important mechanisms are the ones considered here.

Ionization of Surface Groups Dissociation of acidic groups on the surface of a particle will give rise to a negatively charged surface. Conversely, a basic surface will take on a positive charge. In both cases, the magnitude of the surface charge depends on the acidic or basic strengths of the surface groups and on the pH of the solution. The surface charge can be reduced to zero by suppressing surface ionization – by decreasing the pH for negatively charged particles or increasing it for positively charged particles.

Differential Loss of Ions from the Crystal Lattice As an example, consider a crystal of silver iodide placed in water. If equal amounts of Ag+ and I- ions were to dissolve 62

䡲䡲䡲


The liquid layer surrounding the particle exists as two parts; an inner region (Stern layer) where the ions are strongly bound and an outer (diffuse) region where they are less firmly associated. Within the diffuse layer there is a notional boundary inside which the ions and particles form a stable entity. When a particle moves (e.g., due to gravity), ions within the boundary move with it. Those ions beyond the boundary stay with the bulk dispersant. The potential at this boundary (surface of hydrodynamic shear) is the zeta potential (Figure 3). The magnitude of the zeta potential gives an indication of the potential stability of the colloidal system. If all the particles in suspension have a large negative or positive zeta potential then they will tend to repel each other and there is no tendency for the particles to come together. However, if the particles have low zeta potential values then there is no force to prevent the particles coming together and therefore they will flocculate or coagulate.

What This Means for Coatings Historically, coatings have been formulated as solventborne (oil-based paints) or waterborne paints (latex, water-based paints). Environmental requirements limiting VOCs have mandated the reduction of solvent concentration in coating products. Other factors such as ease of use have helped minimize consumer use of oil-based paints. Therefore latex, waterborne paints command an ever-increasing share of the market. It is easy to study zeta potential in these coatings and, because of the additives and formulated nature of the products, manipulating zeta potential is highly relevant as an optimization tool. Specifically, because water has a high surface tension, waterborne paints present unique formulation challenges. It is more difficult to wet the non-polar components of the formulation, such as pigments, etc. Also, because of the physical properties of the oil and polymers used in these aqueous based dispersions, the film formation characteristics of the latex paints themselves tend to be restricted.


3/16/10 2:38:37 PM

Paint Formulations and the Need for Zeta Potential Type ZY Premium Type ZY Type ZS

FIGURE 4 | Zeta potential versus adsorption of a processing aid.

Type Z

®

SiLibeads

King„ of all Beads” strong powerfull

Zeta Potential, [mV]

Type GZ

50 40 30 20 10 0 -10 0 -20 -30

ZP

5

10

15

20

Additive Concentration, [ml] FIGURE 5 | Paint formulation versus zeta potential and surface defects. ZP

Zeta Potential, [mV]

Surface Defects

than just grinding media

300

20

200

10

100

0

0 1

2

3

-10

4 -100

-20

-200

Paint Formulation

nd ess a proc nalysis a cost

ead gh b u o r s th aving ycling s t s co rec rs mina e s g illin ops wet m worksh and

e Pleas s at visit u oating C rican Ame o Sh w 36 6 no.: 1 Stand ril p 5A 13 -1

SIGMUND LINDNER GmbH Oberwarmensteinacher Str. 38 D-95485 Warmensteinach / Germany Phone (++49) 92 77 - 99 40 Fax (++49) 92 77 - 9 94 99 E-Mail: [email protected] www.sili.eu

30

Your innovative and reliable partner for 155 years

Therefore, a variety of additives including surfactants (wetting agents), processing aids and polyelectrolytes, play an important role in latex (waterborne) paint products. As the particle concentration increases during wetting, spreading and coalescence of the coating, the viscosity increases. Based on this scenario, there is a point of phase inversion where the latex particles touch and deform into what will become the continuous phase – the film/coating. The process of film formation goes through four steps: (1) discrete emulsion particles; (2) concentration of the particles or evaporation of the water phase; (3) coalescence where the particles deform; and (4) maturation or diffusion of the chains. Waterborne paints require additives to build the interfacial characteristics to achieve the desired stability for the storage and film formation characteristics needed in the final product. Amongst other properties these include good wetting, uniform film formation, zero defects, specific color, brightness, long-term adhesion and strength. Zeta potential provides a measurement technique that allows the study of latex and pigment components, and also of additives and their possible combinations. Such data provides insight into the particle interfacial structure and allows optimization of each component in the formulation to give the desired final product properties. Figure 4 shows a latex or film former study as a function of a surface-active processing aid. These data represent an initial step


䡲䡲䡲



3/16/10 3:20:36 PM

in understanding how various additives interact with the surface of a film former in a paint formulation. The results indicate that this specific processing aid does adsorb to the surface of the latex, which has a -20 mV zeta potential initially without any additive. It reverses charge and becomes cationic with increased addition of a cationic processing aid. This type of data not only shows surface activity but also indicates the optimal concentration required for the processing aid to be effective. Figure 5 shows a study of a series of paint formulations prepared with the identical latex and pigment components but having different additives. Labeling these formulations as Paint 1 through 4 in the order of the highest negative zeta potential to highest positive zeta potential, and relating zeta potential to coating defects of the final product, a clear trend arises. In this case it indicated that a cationic formulation resulted in fewer defects per 100,000 parts.

dispersed particulates and can be related to the required final product properties. 䡲

References 1. Henry, D.C. Proc.Roy. Soc, 1931, A133, 106. 2. Hunter, R.J. Introduction to Modern Colloid Science, Oxford University Press, 1993. 3. Chevalier, Y., Pichot, C. Graillar, C., Joancot, M., Wong, K., Maquet, J., Lindner, P., and Cabane, B. Colloid & Polymer Sci. 1992, 270, 806. 4. Winnik, M.A. and Wang, Y., J. of Coatings Tech.1992,64 (811), 51. 5. Davidson, G. and Lane, B. Eds. Additives in Waterborne Coatings, RSC, 2003. 6. Conley, R. F. Practical Dispersion: A Guide to Understanding and Formulating Slurries, VCH Pub. Inc., 1996.

For more information, visit www.malvern.com or call 508/768.6400.

Conclusion In conclusion, paints are multi-component systems formulated to produce specific product properties. The rate and uniformity at which these coatings wet spread and coalesce into a film can be controlled by the chemical components used in the formulation. Coatings, depending on their end use, are complex formulations with a minimum of four components added into a dispersed mixture. Zeta potential measurements provide insight into the stability of the latex and pigments in the dispersion. Zeta potential also helps to elucidate the interfacial characteristics of the

For AC Show coverage visit: www.pcimag.com/ac_show Or follow our coverage on Twitter.

Pioneering Sustainable Change Cytec Coating Resins delivers innovative products beyond our customer’s imagination. We are pioneers in the development and production of high performance coating solutions. Our line of low-VOC coatings, radiation curing and powder coating resins and additives allow our customers to create sustainable change for the industries they serve. For more information, visit us at the American Coatings Show in booth #2625.

Email: [email protected]

l

Worldwide Contact information: www.cytec.com

l

US Toll Free: 800-652-6013

l

Tel: 973-357-3193

© 2010 Cytec Industries Inc. All Rights Reserved.

Visit ads.pcimag.com PA I N T & C O A T I N G S I N D U S T R Y


䡲䡲䡲

65

3/16/10 2:38:58 PM

Alkyd Latexes: Opening the Door for a Greener Tomorrow

A

s environmental regulations and the “go green” era continue to be the driving force of current coatings resin development, the importance of having a versatile, low-VOC resin is evident. With the chemical industry affected by the economic crisis that is being experienced globally, many companies have downsized their staff, production and research capabilities. This makes it hard for paint companies to delve into new research areas, as they are constantly reformulating product lines to meet current and future acceptable VOC levels as they also strive for “green” certification. The green certification process, available from a variety of independent third parties, is offered to companies and regarded as a positive from many consumers’ perspectives and has become a crucial part of new product development for several industries. These certification programs have a list of certain criteria that are required for a product to boast their stamp of approval. In addition, existing and novel coatings products must continue to meet allowable levels of VOCs in both architectural and industrial paints that vary from region to region. As the uncertainty of the economic situation continues, wouldn’t it be nice to have a multipurpose resin that can be used in multiple applications that easily meets current and future VOC allowances and qualifies for green certification?

Green Certification Programs While the environmental component emerges as an important aspect in a consumer’s decision, certification

programs have been developed to help ensure the environmental benefits of specific products. These certifications are offered by independent third parties and typically entail a detailed certification process. Most programs for the coatings industry are focused on chemical exemptions, VOC limits, performance requirements and packaging constraints. Currently, reputable programs for a broad range of products, including coatings products, are Green Seal, Ecologo and the Coatings Research Group, Inc.’s Green Wise. Other programs exist, but are targeted toward specific market segments. Table 1 provides a summary of the certification plans and criteria for different coatings applications. All of the certification programs outlined in Table 1 are currently the most frequently used across the coatings industry. It is evident the renewable resource content of the product does not play a role in any of these certification processes. As more of these organizations are developed and the definition of what characterizes a green product continues to evolve, one can presuppose that in the future the renewable resource content of a product will be pertinent for green certification.

History of Alkyds Alkyd chemistry has been a strong force in the coatings industry for many years. The chemistry, although very established, still has room for growth as the focus on materials from renewable resources continues to develop. Although alkyds have predominantly been available in organic vehicles, the thrust to develop supe-

By Jamie Dziczkowski, Ph.D., Chemist Associate, Coatings Technology | Reichhold, Inc., Research Triangle Park, NC 66

䡲䡲䡲

066 Reichhold FT.indd 66


3/16/10 2:30:50 PM


rior waterborne alkyds has been set in motion. Waterborne alkyd technologies including water reducible alkyds, alkyd dispersions, and alkyd latexes have been commercially available for several decades. Although still possessing some of the positive attributes of alkyd resins, these first-generation waterborne alkyds were inferior to the acrylic latex due to their poor hydrolytic stability. Today, several large resin suppliers have brought a number of alkyd dispersions and alkyd latexes to the table that mimic solventborne alkyd performance while providing desired hydrolytic stability. One attractive component of alkyd chemistry is the ability for oxidation that is contributed from the oil component of the polymer. Oxidation occurs through the unsaturated moieties that are found along the pendant fatty acid chains. The benefits presented by an oxidizable system are evident. With an alkyd-bound coating, the

initial film exhibits good flow and leveling characteristics due to the low molecular weight, low glass transition temperature (Tg) and flexibility of the polymer chains. Then, following air crosslinking, the final film exhibits good adhesion, hardness, gloss and corrosion resistance. The film formation for an alkyd resin is depicted in Figure 1. By starting with a low-molecular-weight polymer, the lack of coalescent helps keep the VOC to a minimum when moving to an aqueous carrier.

Using Alkyd Latexes to Achieve Green Products New-generation alkyd latexes, including the Beckosol® AQ line of alkyd latexes currently available from Reichhold, are made by the introduction of external surfactants and advanced processing techniques that offer a stable latex in a continuous aqueous phase. These stable latexes are achieved by careful selection of the surfactant system

TABLE 1 | Certification plans and criteria summary for coatings applications. Company Green Seal

Ecologo

Green Wise (CRGI 1)

Green Guard Institute

Standard #/Key Requirements2

Product Type

Floor Care Prducts

GS-40 Specific performance requirements, nontoxic, non-corrosive, nonsensitizing, FP > 150 °C, recyclable packaging, no APE's or heavy metals

CCD-147 Specific performance requirements, VOC limits, no halogenated solvents, no isocyanate or polymers of urethane, free monomer content < 50 ppm, pH < 12.5, be biodegradable as described

na

na

Paints/ Coatings

GS-11 Specific performance requirements, compound prohibitions (APEs, phthalates, heavy metals), VOC limits, conusmer education, packaging/ labeling

CCD-047 Specific performance requirements, no aromatic or halogenated compounds, no formaldehyde, MEK, or AN, FP > 142 °C, VOC limits

CRGI Green Wise Specific performance requirements depending on type of paint, VOC limits, chemical component limitations (no aromatics, phthalates, MEK, heavy metals)

GGPS.EC.016 Allowable limits of styrene, formaldehyde, and aldehydes, VOC levels must meet (SCAQMD) Rule #1113, top coats must meet Green Seal Standard GS-11, anticorrosive paints must meet chemical requirements of Green Seal Standard GS-03

RecycledContent Latex Paints

GS-43 Specific performance requirements, compound prohibitions (aromatics, phthalates, metals, ketones), VOC limits

CCD-048 Specific performance requirements, > 50% post consumer material by volume, na chemical prohibitions ( APEs, aromatics, MEK, metals), FP > 142 °C, VOC limits

Stains and Finishes

GS-47 Specific performance requirements, compound prohibitions (APEs, phthalates, metals, halogenated solvents), VOC limits, VAC limits, packaging requirements

See Paints and Coatings Specifications (CCD-047)

CRGI Green Wise Specific performance requirements depending on type of paint, VOC limits, chemical component limitations (no aromatics, phthalates, MEK, heavy metals)

na

GGPS.EC.016 Allowable limits of styrene, formaldehyde, and aldehydes, VOC levels must meet (SCAQMD) Rule #1113, top coats must meet Green Seal Standard GS-11, anticorrosive paints must meet chemical requirements of Green Seal Standard GS-03

1

Coatings Research Group, Inc. Summary of requirements. For detailed qualifications please visit the corresponding website. http://www.greenseal.org/ http://www.terrachoice-certified.com/en/ http://www.greenwisepaint.com/performance-standards.aspx http://www.greenguard.org/

2

68

䡲䡲䡲

066 Reichhold FT.indd 68


3/16/10 2:31:01 PM


FIGURE 1 | Benefits of oxidation in an alkyd system.

Alkyd - low MW & flexible polymer chain

O2 + driers

Crosslinking

Excellent wetting due to low MW and low Tg Air-crosslinking to build molecular weight and coating performance and precise control of the emulsion process. A key factor for stabilization is attaining small emulsion particle diameters. The quality of the latex is dependent on the surface tension present in the particles. Alkyd latexes can be prepared by either direct emulsification or a phase inversion process. By achieving stable emulsions through the introduction of a protective surfactant shell, the core

alkyd resin is stabilized and hydrolysis rates are hindered. This type of system addresses the VOC issue and provides the benefits of a traditional alkyd resin. See Figure 2 for a pictorial description of an alkyd binder in a latex paint stabilized by an outer protective layer. One benefit of alkyd latex-based paint is once the coating is applied, the low-molecular-weight, low-Tg alkyd resin crosslinks through the traditional oxidative crosslinking mechanism characteristic of alkyd resins. This eliminates the need for expensive coalescing solvents and additives that are needed in acrylic latex paints in order to get excellent application properties. Another benefit of alkyd latexes is that it formulates like a typical latex paint. Standard latex rheological additives, dispersants and defoamers are effective in developing alkyd latex paints. Thus, once a system is established with an alkyd latex, formulating chemists will have more time to spend on new R&D instead of reformulating. This is all a result of the

Paint & Coatings Industry 2010,04

Paint & Coatings Industry 2010,09

Paint & Coatings Industry 2010,03

Paint & Coatings Industry 2010,06

Paint & Coatings Industry Supplier Handbook 2012

Paint & Coatings Industry February 2012

Paint & Coatings Industry 2010, 08

Paint & Coating Industry Coatings Supplier Handbook 2011

Paint & Coating Industry April 2011

Paint & Coating Industry July 2011

Paint & Coating Industry February 2011

Paint & Coating Industry November 2011

Paint & Coating Industry May 2011

Paint & Coating Industry August 2011

Paint & Coating Industry September 2011

Paint & Coating Industry October 2011

Paint & Coating Industry December 2011

Paint & Coating Industry January 2011

Paint & Coating Industry March 2011

Paint & Coating Industry June 2011

Paint and Surface Coatings: Theory and Practice

Paint and Coatings: Applications and Corrosion Resistance (Corrosion Technology)

Printing Ink and Overprint Varnish Formulations, 2nd Edition, Second Edition (Paint & Coatings)

Printing Ink and Overprint Varnish Formulations, 2nd Edition, Second Edition (Paint & Coatings)

Paint Shop Pro 8 Fast & Easy

Coatings Materials and Surface Coatings

Adhesives, Sealants and Coatings for the Electronics Industry

Resins for Surface Coatings. Alkyds & Polyesters

Wet Paint

Coatings Tribology

Wet Paint

Paint & Coatings Industry 2010,04

Paint & Coatings Industry 2010,09

Paint & Coatings Industry 2010,03

Paint & Coatings Industry 2010,06

Paint & Coatings Industry Supplier Handbook 2012

Paint & Coatings Industry February 2012

Paint & Coatings Industry 2010, 08

Paint & Coating Industry Coatings Supplier Handbook 2011

Paint & Coating Industry April 2011

Paint & Coating Industry July 2011

Paint & Coating Industry February 2011

Paint & Coating Industry November 2011

Paint & Coating Industry May 2011

Paint & Coating Industry August 2011

Paint & Coating Industry September 2011

Paint & Coating Industry October 2011

Paint & Coating Industry December 2011

Paint & Coating Industry January 2011

Paint & Coating Industry March 2011

Paint & Coating Industry June 2011

Paint and Surface Coatings: Theory and Practice

Paint and Coatings: Applications and Corrosion Resistance (Corrosion Technology)

Printing Ink and Overprint Varnish Formulations, 2nd Edition, Second Edition (Paint & Coatings)

Printing Ink and Overprint Varnish Formulations, 2nd Edition, Second Edition (Paint & Coatings)

Paint Shop Pro 8 Fast & Easy

Coatings Materials and Surface Coatings

Adhesives, Sealants and Coatings for the Electronics Industry

Resins for Surface Coatings. Alkyds & Polyesters